Propriétés techniques
Backing material | none |
Color | white |
Color of liner | white |
Thickness of liner | 127 µm |
Total thickness | 250 µm |
Type of adhesive | type: acrylic |
Type of liner | type: PE-coated paper |
Backing material | none |
Color | white |
Color of liner | white |
Thickness of liner | 127 µm |
Total thickness | 250 µm |
Type of adhesive | type: acrylic |
Type of liner | type: PE-coated paper |
Backing material | none |
Color | white |
Color of liner | white |
Thickness of liner | 127 µm |
Total thickness | 250 µm |
Type of adhesive | type: acrylic |
Type of liner | type: PE-coated paper |
Release of liner | easy |
Temperature resistance (125°C) | very good |
Density | 1.73 g/cm³ |
Volume resistance | 1000000000000 Ohm.cm |
Breakdown voltage | 7.4 KV |
Flame retardancy | V2 |
Surface resistance | 1000000000000 10^6 Ohm |
Hardness - Shore 00 | 70 STK |
Temperature resistance short term | 200 °C |
Temperature resistance (-40°C) | very good |
Thermal conductivity z-direction | 0.8 W/mK |
Release of liner | easy |
Temperature resistance (125°C) | very good |
Density | 1.73 g/cm³ |
Volume resistance | 1000000000000 Ohm.cm |
Breakdown voltage | 7.4 KV |
Flame retardancy | V2 |
Surface resistance | 1000000000000 10^6 Ohm |
Hardness - Shore 00 | 70 STK |
Temperature resistance short term | 200 °C |
Temperature resistance (-40°C) | very good |
Thermal conductivity z-direction | 0.8 W/mK |
Adhesion to Aluminium (20 min. @ RT, 90°) | 2.6 N/cm |
Adhesion to Aluminium (after 3 days) | 5.8 N/cm |
Adhesion to Aluminium (20 min. @ RT, 90°) | 2.6 N/cm |
Adhesion to Aluminium (after 3 days) | 5.8 N/cm |