Product Construction
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 160 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
160 µm double sided translucent premium non woven tape
tesa® 4962 is a double-sided non-woven industrial mounting and splicing tape with a highly tackified acrylic adhesive. The premium non-woven tape is, for instance, used for mounting signs and nameplates or other mounting and high-performance lamination applications. tesa® 4962 is especially designed to connect flexible materials to one another. The mounting and splicing tape is able to withstand numerous environmental factors such as humidity, UV light, and temperatures of up to 200°C for limited periods of time. The tackified acrylic adhesive offers excellent hold on various surfaces, very high tack, and good shear strength. The adhesive is coated on a flexible and conformable cellulose non-woven backing that even conforms to difficult 3D shapes.
tesa® 4962 is also available in a 100 µm version (tesa® 4959).
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 160 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Backing material | non-woven |
Color | translucent |
Color of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 160 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Elongation at break | 3 % |
Tensile strength | 8 N/cm |
Ageing resistance (UV) | very good |
Tack | very good |
Temperature resistance short term | 200 °C |
Static shear resistance at 23°C | good |
Temperature resistance min. | -40 °C |
Fogging | good |
Humidity resistance | very good |
Chemical resistance | good |
Static shear resistance at 40°C | medium |
Temperature resistance long term | 80 °C |
Elongation at break | 3 % |
Tensile strength | 8 N/cm |
Ageing resistance (UV) | very good |
Tack | very good |
Temperature resistance short term | 200 °C |
Static shear resistance at 23°C | good |
Temperature resistance min. | -40 °C |
Fogging | good |
Humidity resistance | very good |
Chemical resistance | good |
Static shear resistance at 40°C | medium |
Temperature resistance long term | 80 °C |
Adhesion to ABS (initial) | 11 N/cm |
Adhesion to ABS (after 14 days) | 12 N/cm |
Adhesion to Aluminium (initial) | 10 N/cm |
Adhesion to Aluminium (after 14 days) | 10.5 N/cm |
Adhesion to PC (initial) | 13 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PC (covered side, after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 6.5 N/cm |
Adhesion to PE (after 14 days) | 7 N/cm |
Adhesion to PET (initial) | 9.5 N/cm |
Adhesion to PET (after 14 days) | 10.5 N/cm |
Adhesion to PP (initial) | 8.5 N/cm |
Adhesion to PP (after 14 days) | 10 N/cm |
Adhesion to PS (initial) | 12 N/cm |
Adhesion to PS (after 14 days) | 13 N/cm |
Adhesion to PVC (initial) | 11 N/cm |
Adhesion to PVC (after 14 days) | 15 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 12 N/cm |
Adhesion to ABS (initial) | 11 N/cm |
Adhesion to ABS (after 14 days) | 12 N/cm |
Adhesion to Aluminium (initial) | 10 N/cm |
Adhesion to Aluminium (after 14 days) | 10.5 N/cm |
Adhesion to PC (initial) | 13 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PC (covered side, after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 6.5 N/cm |
Adhesion to PE (after 14 days) | 7 N/cm |
Adhesion to PET (initial) | 9.5 N/cm |
Adhesion to PET (after 14 days) | 10.5 N/cm |
Adhesion to PP (initial) | 8.5 N/cm |
Adhesion to PP (after 14 days) | 10 N/cm |
Adhesion to PS (initial) | 12 N/cm |
Adhesion to PS (after 14 days) | 13 N/cm |
Adhesion to PVC (initial) | 11 N/cm |
Adhesion to PVC (after 14 days) | 15 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 12 N/cm |