Product Construction
Backing material | PET film |
Color | transparent |
Total thickness | 200 µm |
Type of adhesive | acrylic |
200µm double sided transparent PET film tape with 90% PCR PET content in backing
tesa® 51966 is a transparent, double-sided industrial mounting tape with a 90% post-consumer recycled (PCR) PET backing and a highly tackified acrylic adhesive. The double-sided tape is especially designed for the converter and tape specialist business and is able to withstand numerous environmental factors such as humidity, UV light, and temperatures of up to 130°C for limited periods of time. The tackified acrylic adhesive provides excellent adhesion on various surfaces, very high tack, and good shear strength.
tesa® 51966 contains an average of 8% post-consumer recycled content, consisting of 90% recycled PET backing. Liner and tape core are considered packaging materials and are excluded from recycled content calculations. This is a third-party environmental claim validated against the UL Environmental Claim Validation Procedure 2809 for recycled content. The UL Environmental Claim Validation Program falls under UL’s ISO/IEC 17025 accreditation. Find more information on the UL SPOT® database
https://spot.ul.com/main-app/products/detail/62a340de7501b678a13670cb?page_type=Products%20Catalog
Backing material | PET film |
Color | transparent |
Total thickness | 200 µm |
Type of adhesive | acrylic |
Backing material | PET film |
Color | transparent |
Total thickness | 200 µm |
Type of adhesive | acrylic |
Elongation at break | 55 % |
Tensile strength | 20 N/cm |
Temperature resistance min. | -40 °C |
Tack | very good |
Temperature resistance short term | 130 °C |
Static shear resistance at 40°C | good |
Ageing resistance (UV) | good |
Static shear resistance at 23°C | good |
Softener resistance | good |
Chemical resistance | good |
Temperature resistance long term | 80 °C |
Humidity resistance | very good |
Elongation at break | 55 % |
Tensile strength | 20 N/cm |
Temperature resistance min. | -40 °C |
Tack | very good |
Temperature resistance short term | 130 °C |
Static shear resistance at 40°C | good |
Ageing resistance (UV) | good |
Static shear resistance at 23°C | good |
Softener resistance | good |
Chemical resistance | good |
Temperature resistance long term | 80 °C |
Humidity resistance | very good |
Adhesion to ABS (initial) | 10.5 N/cm |
Adhesion to ABS (after 14 days) | 11.5 N/cm |
Adhesion to Aluminium (initial) | 9 N/cm |
Adhesion to Aluminium (after 14 days) | 10 N/cm |
Adhesion to PC (initial) | 13 N/cm |
Adhesion to PC (after 14 days) | 13.5 N/cm |
Adhesion to PE (initial) | 7 N/cm |
Adhesion to PE (after 14 days) | 7.5 N/cm |
Adhesion to PET (initial) | 9 N/cm |
Adhesion to PET (after 14 days) | 9.5 N/cm |
Adhesion to PP (initial) | 7.5 N/cm |
Adhesion to PP (after 14 days) | 8 N/cm |
Adhesion to PS (initial) | 11 N/cm |
Adhesion to PS (after 14 days) | 12 N/cm |
Adhesion to PVC (initial) | 9 N/cm |
Adhesion to PVC (after 14 days) | 13 N/cm |
Adhesion to Steel (initial) | 10.5 N/cm |
Adhesion to Steel (after 14 days) | 11 N/cm |
Adhesion to ABS (initial) | 10.5 N/cm |
Adhesion to ABS (after 14 days) | 11.5 N/cm |
Adhesion to Aluminium (initial) | 9 N/cm |
Adhesion to Aluminium (after 14 days) | 10 N/cm |
Adhesion to PC (initial) | 13 N/cm |
Adhesion to PC (after 14 days) | 13.5 N/cm |
Adhesion to PE (initial) | 7 N/cm |
Adhesion to PE (after 14 days) | 7.5 N/cm |
Adhesion to PET (initial) | 9 N/cm |
Adhesion to PET (after 14 days) | 9.5 N/cm |
Adhesion to PP (initial) | 7.5 N/cm |
Adhesion to PP (after 14 days) | 8 N/cm |
Adhesion to PS (initial) | 11 N/cm |
Adhesion to PS (after 14 days) | 12 N/cm |
Adhesion to PVC (initial) | 9 N/cm |
Adhesion to PVC (after 14 days) | 13 N/cm |
Adhesion to Steel (initial) | 10.5 N/cm |
Adhesion to Steel (after 14 days) | 11 N/cm |