Product Construction
Backing material | PVC film |
Colour | white |
Colour of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 295 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Double-sided filmic tape
tesa® 4968 is a white double-sided self-adhesive tape consisting of a PVC-backing and a tackified acrylic adhesive.
tesa® 4968 features especially:
Backing material | PVC film |
Colour | white |
Colour of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 295 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Backing material | PVC film |
Colour | white |
Colour of liner | brown |
Thickness of liner | 69 µm |
Total thickness | 295 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Elongation at break | 130 % |
Tensile strength | 30 N/cm |
Softener resistance | very good |
Temperature resistance long term duration | 60 °C |
Temperature resistance min. | -40 °C |
Static shear resistance at 40°C | medium |
Humidity resistance | very good |
Chemical resistance | good |
Static shear resistance at 23°C | good |
Temperature resistance short term duration | 70 °C |
Ageing resistance (UV) | good |
Tack | very good |
Elongation at break | 130 % |
Tensile strength | 30 N/cm |
Softener resistance | very good |
Temperature resistance long term duration | 60 °C |
Temperature resistance min. | -40 °C |
Static shear resistance at 40°C | medium |
Humidity resistance | very good |
Chemical resistance | good |
Static shear resistance at 23°C | good |
Temperature resistance short term duration | 70 °C |
Ageing resistance (UV) | good |
Tack | very good |
Adhesion to ABS (initial) | 13.1 N/cm |
Adhesion to ABS (after 14 days) | 20 N/cm |
Adhesion to Aluminium (initial) | 10.3 N/cm |
Adhesion to Aluminium (after 14 days) | 20.7 N/cm |
Adhesion to PC (initial) | 13.8 N/cm |
Adhesion to PC (after 14 days) | 24.6 N/cm |
Adhesion to PET (initial) | 9.6 N/cm |
Adhesion to PET (after 14 days) | 12.7 N/cm |
Adhesion to PP (initial) | 11 N/cm |
Adhesion to PP (after 14 days) | 14.1 N/cm |
Adhesion to PS (initial) | 11.9 N/cm |
Adhesion to PS (after 14 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 10.6 N/cm |
Adhesion to PVC (after 14 days) | 25.3 N/cm |
Adhesion to Steel (initial) | 12.5 N/cm |
Adhesion to Steel (after 14 days) | 21.2 N/cm |
Adhesion to ABS (initial) | 13.1 N/cm |
Adhesion to ABS (after 14 days) | 20 N/cm |
Adhesion to Aluminium (initial) | 10.3 N/cm |
Adhesion to Aluminium (after 14 days) | 20.7 N/cm |
Adhesion to PC (initial) | 13.8 N/cm |
Adhesion to PC (after 14 days) | 24.6 N/cm |
Adhesion to PET (initial) | 9.6 N/cm |
Adhesion to PET (after 14 days) | 12.7 N/cm |
Adhesion to PP (initial) | 11 N/cm |
Adhesion to PP (after 14 days) | 14.1 N/cm |
Adhesion to PS (initial) | 11.9 N/cm |
Adhesion to PS (after 14 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 10.6 N/cm |
Adhesion to PVC (after 14 days) | 25.3 N/cm |
Adhesion to Steel (initial) | 12.5 N/cm |
Adhesion to Steel (after 14 days) | 21.2 N/cm |