Product Construction
Backing material | none |
Colour | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 130 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
130 µm reinforced water-based acrylic adhesive layer with PET scrim for mounting applications in automotive interiors
tesa® 66013 is a conformable, water-based acrylic adhesive tape with a thickness of 130 µm, reinforced by a PET scrim. This tape has especially been developed for all kinds of demanding lamination and mounting applications. Due to its low VOC property it is particularly designed to meet automotive interior requirements.
tesa® 66013 is suitable for laminating all kinds of foam, fleece, and felt substrates and mounting light interior components.
This product is also available in 75 µm(tesa® 66007) and 220 µm (tesa® 66022).
Backing material | none |
Colour | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 130 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Backing material | none |
Colour | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 130 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Temperature resistance max. | 180 °C |
Low VOC | very good |
Suitable for rough surfaces | very good |
Suitable for die cutting | yes |
Fogging | very good |
Temperature resistance min. | -40 °C |
Tack | very good |
Temperature resistance max. | 180 °C |
Low VOC | very good |
Suitable for rough surfaces | very good |
Suitable for die cutting | yes |
Fogging | very good |
Temperature resistance min. | -40 °C |
Tack | very good |
Adhesion to ABS (initial) | 14.5 N/cm |
Adhesion to ABS (after 3 days) | 14.5 N/cm |
Adhesion to PC (initial) | 14.5 N/cm |
Adhesion to PC (after 3 days) | 15.1 N/cm |
Adhesion to PE (initial) | 5.9 N/cm |
Adhesion to PE (after 3 days) | 7.2 N/cm |
Adhesion to PET (initial) | 13.9 N/cm |
Adhesion to PET (after 3 days) | 15.3 N/cm |
Adhesion to PP (initial) | 8 N/cm |
Adhesion to PP (after 3 days) | 12 N/cm |
Adhesion to PS (initial) | 14.6 N/cm |
Adhesion to PS (after 3 days) | 14.9 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 14.3 N/cm |
Adhesion to Steel (initial) | 15.4 N/cm |
Adhesion to Steel (after 3 days) | 16.5 N/cm |
Adhesion to ABS (initial) | 14.5 N/cm |
Adhesion to ABS (after 3 days) | 14.5 N/cm |
Adhesion to PC (initial) | 14.5 N/cm |
Adhesion to PC (after 3 days) | 15.1 N/cm |
Adhesion to PE (initial) | 5.9 N/cm |
Adhesion to PE (after 3 days) | 7.2 N/cm |
Adhesion to PET (initial) | 13.9 N/cm |
Adhesion to PET (after 3 days) | 15.3 N/cm |
Adhesion to PP (initial) | 8 N/cm |
Adhesion to PP (after 3 days) | 12 N/cm |
Adhesion to PS (initial) | 14.6 N/cm |
Adhesion to PS (after 3 days) | 14.9 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 14.3 N/cm |
Adhesion to Steel (initial) | 15.4 N/cm |
Adhesion to Steel (after 3 days) | 16.5 N/cm |