Product Construction
Bahan penyangga | PET |
Jenis Liner | PE-coated paper |
Jenis Perekat | tackified acrylic |
Ketebalan liner | 140 µm |
Ketebalan total | 150 µm |
Warna | transparent |
Warna liner | white/blue logo |
150µm double coated PET tape
tesa® 88663 is a transparent, double coated self-adhesive tape consisting of a PET backing and a tackified acrylic adhesive specifically designed for Industrial Trade & Converting market. It is the ideal solution for multi-purpose laminating and converting applications.
Bahan penyangga | PET |
Jenis Liner | PE-coated paper |
Jenis Perekat | tackified acrylic |
Ketebalan liner | 140 µm |
Ketebalan total | 150 µm |
Warna | transparent |
Warna liner | white/blue logo |
Bahan penyangga | PET |
Jenis Liner | PE-coated paper |
Jenis Perekat | tackified acrylic |
Ketebalan liner | 140 µm |
Ketebalan total | 150 µm |
Warna | transparent |
Warna liner | white/blue logo |
Perpanjangan saat putus | 50 % |
Kekuatan tarik | 40 N/cm |
Durasi ketahanan suhu jangka pendek | 200 °C |
Ketahanan terhadap geser statis pada 23 °C | very good |
Paku payung | medium |
Ketahanan terhadap geser statis pada 70 °C | good |
Durasi ketahanan suhu jangka panjang | 95 °C |
Perpanjangan saat putus | 50 % |
Kekuatan tarik | 40 N/cm |
Durasi ketahanan suhu jangka pendek | 200 °C |
Ketahanan terhadap geser statis pada 23 °C | very good |
Paku payung | medium |
Ketahanan terhadap geser statis pada 70 °C | good |
Durasi ketahanan suhu jangka panjang | 95 °C |
Daya rekat ke ABS (awal) | 11 N/cm |
Daya rekat ke ABS (setelah 14 hari) | 13.2 N/cm |
Daya rekat ke PC (awal) | 11.1 N/cm |
Daya rekat ke PC (setelah 14 hari) | 15.3 N/cm |
Daya rekat ke PE (awal) | 4.6 N/cm |
Daya rekat ke PE (setelah 14 hari) | 5.2 N/cm |
Daya rekat ke PET (awal) | 11.3 N/cm |
Daya rekat ke PET (setelah 14 hari) | 12.9 N/cm |
Daya rekat ke PP (awal) | 2.8 N/cm |
Daya rekat ke PP (setelah 14 hari) | 5.3 N/cm |
Daya rekat ke Baja (awal) | 11.6 N/cm |
Daya rekat ke Baja (setelah 14 hari) | 13.8 N/cm |
Daya rekat ke ABS (awal) | 11 N/cm |
Daya rekat ke ABS (setelah 14 hari) | 13.2 N/cm |
Daya rekat ke PC (awal) | 11.1 N/cm |
Daya rekat ke PC (setelah 14 hari) | 15.3 N/cm |
Daya rekat ke PE (awal) | 4.6 N/cm |
Daya rekat ke PE (setelah 14 hari) | 5.2 N/cm |
Daya rekat ke PET (awal) | 11.3 N/cm |
Daya rekat ke PET (setelah 14 hari) | 12.9 N/cm |
Daya rekat ke PP (awal) | 2.8 N/cm |
Daya rekat ke PP (setelah 14 hari) | 5.3 N/cm |
Daya rekat ke Baja (awal) | 11.6 N/cm |
Daya rekat ke Baja (setelah 14 hari) | 13.8 N/cm |
Unduh file di bawah ini untuk detail teknis dan informasi lebih lanjut tentang produk ini.