Product Construction
Backing material | PET |
Colour | transparent |
Colour of liner | brown/blue logo |
Total thickness | 100 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
tesa® 58362 is a 100μm double-sided transparent PET filmic tape
The tackified acrylic adhesive gives this product a good peel strength and very high dynamic shear between two polar substrates. The 50μm transparent PET filmic backing offers excellent electrical insulation property. The glassine liner ensures it can be easily released without adhesive residue. It can meet the strict automotive environmental and long-term durability requirement.
Backing material | PET |
Colour | transparent |
Colour of liner | brown/blue logo |
Total thickness | 100 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
Backing material | PET |
Colour | transparent |
Colour of liner | brown/blue logo |
Total thickness | 100 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
Temperature range | -40~125 |
Static shear resistance at 40°C | very good |
Dielectric breakdown voltage | 9800 V |
Static shear resistance at 70°C | very good |
Temperature resistance long term duration | 125 °C |
Static shear resistance at 23°C | very good |
Temperature resistance | very good |
Temperature range | -40~125 |
Static shear resistance at 40°C | very good |
Dielectric breakdown voltage | 9800 V |
Static shear resistance at 70°C | very good |
Temperature resistance long term duration | 125 °C |
Static shear resistance at 23°C | very good |
Temperature resistance | very good |
Adhesion to Aluminium (initial) | 5.7 N/cm |
Adhesion to PC (initial) | 6.7 N/cm |
Adhesion to Steel (initial) | 7 N/cm |
Adhesion to Steel (after 14 days) | 8.5 N/cm |
Adhesion to Aluminium (initial) | 5.7 N/cm |
Adhesion to PC (initial) | 6.7 N/cm |
Adhesion to Steel (initial) | 7 N/cm |
Adhesion to Steel (after 14 days) | 8.5 N/cm |