Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | transparent |
| Total thickness | 205 µm |
tesa® 6965 Next Gen - Team 4965 Fingerlift
205µm double sided transparent PET film tape with fingerlift
Sustainable Aspects
- tesa® 6965 Next Gen with -39% CO₂ emissions1 compared to tesa® 6965
- Biomass balanced tackified acrylic adhesive
- 90% PCR PET in the backing
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
- Recycling friendly according to the INGEDE method
Product description
tesa® 6965 - Team 4965 Fingerlift is a transparent, double-sided industrial mounting tape with fingerlift consisting of a PET backing and a modified acrylic adhesive. The double-sided mounting tape is a fingerlift version of tesa® 4965 Original and its adhesive is based on a patented and protected product technology. tesa® 6965 - Team 4965 Fingerlift is used in various different industries, frequently used for closing corrugated-board cartons or mounting different profiles. The tackified acrylic adhesive provides reliable bonding performance even at high temperatures and on rough carboard surfaces. tesa® 6965 - Team 4965 Fingerlift comes with a fingerlift (extended liner) for convenient liner removal and is recycling friendly according to the INGEDE method.
Several products are equipped with this unique and high-performing product design. Together, these products make up Team 4965. This double-sided film tape assortment helps to easily select the most efficient tape based on customer demands, products, and processes. Explore the benefits of the full tesa® 4965 assortment here:
https://www.tesa.com/en/industry/general-applications/mounting/team-4965-assortment
Product details and specifications
Product Features
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
- Recycling friendly according to the INGEDE method
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
- Immediate usability right after assembly
- Reliable bonding performance even at high temperatures and on rough corrugated-board surfaces
- Low VOC – measured according to VDA 278 analysis
Application Fields
- tesa® 6965 - Team 4965 Fingerlift is especially designed for the closure of corrugated-board cartons
- Rubber/EPDM profile mounting
- Mounting decorative profiles and moldings in the furniture industry
- ABS plastic parts mounting in the car industry
Sustainable Aspects
- tesa® 6965 Next Gen with -39% CO₂ emissions1 compared to tesa® 6965
- Biomass balanced tackified acrylic adhesive
- 90% PCR PET in the backing
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | transparent |
| Total thickness | 205 µm |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Chemical Resistance | good |
| Temperature resistance long term | 100 °C |
| Humidity resistance | very good |
| Temperature resistance short term | 200 °C |
| Temperature resistance min. | -40 °C |
| Tack | good |
| Softener resistance | good |
| Static shear resistance at 40°C | very good |
| Ageing resistance (UV) | good |
| Static shear resistance at 23°C | very good |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Chemical Resistance | good |
| Temperature resistance long term | 100 °C |
| Humidity resistance | very good |
| Temperature resistance short term | 200 °C |
| Temperature resistance min. | -40 °C |
| Tack | good |
| Softener resistance | good |
| Static shear resistance at 40°C | very good |
| Ageing resistance (UV) | good |
| Static shear resistance at 23°C | very good |
Adhesion to Values
| Adhesion to ABS (initial) | 10.3 N/cm |
| Adhesion to ABS (after 14 days) | 12 N/cm |
| Adhesion to Aluminium (initial) | 9.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14 N/cm |
| Adhesion to PE (initial) | 5.8 N/cm |
| Adhesion to PE (after 14 days) | 6.9 N/cm |
| Adhesion to PET (initial) | 9.2 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PP (initial) | 6.8 N/cm |
| Adhesion to PP (after 14 days) | 7.9 N/cm |
| Adhesion to PS (initial) | 10.6 N/cm |
| Adhesion to PS (after 14 days) | 12 N/cm |
| Adhesion to PVC (initial) | 8.7 N/cm |
| Adhesion to PVC (after 14 days) | 13 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 11.8 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 10.3 N/cm |
| Adhesion to ABS (after 14 days) | 12 N/cm |
| Adhesion to Aluminium (initial) | 9.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14 N/cm |
| Adhesion to PE (initial) | 5.8 N/cm |
| Adhesion to PE (after 14 days) | 6.9 N/cm |
| Adhesion to PET (initial) | 9.2 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PP (initial) | 6.8 N/cm |
| Adhesion to PP (after 14 days) | 7.9 N/cm |
| Adhesion to PS (initial) | 10.6 N/cm |
| Adhesion to PS (after 14 days) | 12 N/cm |
| Adhesion to PVC (initial) | 8.7 N/cm |
| Adhesion to PVC (after 14 days) | 13 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 11.8 N/cm |
Additional Info
Liner variants:
Low VOC – measured according to VDA 278 analysis, tesa® 6965 - Team 4965 Fingerlift does not contain any single substances restricted by the drafted GB regulations (China).
- PV0: red MOPP film (80μm; 72g/m²)
- PV2: brown glassine paper (78μm; 90g/m²)
- PV8: white MOPP friction liner (80μm; 72g/m²)
Low VOC – measured according to VDA 278 analysis, tesa® 6965 - Team 4965 Fingerlift does not contain any single substances restricted by the drafted GB regulations (China).
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.