Product Construction
Backing material | PP film |
Colour | white |
Total thickness | 240 µm |
Type of adhesive | acrylic |
Double-sided filmic tape
tesa® 64993 is a white double-sided self-adhesive tape consisting of a PP-film backing and a tackified acrylic adhesive.
Backing material | PP film |
Colour | white |
Total thickness | 240 µm |
Type of adhesive | acrylic |
Backing material | PP film |
Colour | white |
Total thickness | 240 µm |
Type of adhesive | acrylic |
Elongation at break | 20 % |
Tensile strength | 130 N/cm |
Static shear resistance at 40°C | medium |
Ageing resistance (UV) | good |
Tack | good |
Chemical resistance | good |
Softener resistance | good |
Temperature resistance short term duration | 120 °C |
Humidity resistance | very good |
Static shear resistance at 23°C | good |
Elongation at break | 20 % |
Tensile strength | 130 N/cm |
Static shear resistance at 40°C | medium |
Ageing resistance (UV) | good |
Tack | good |
Chemical resistance | good |
Softener resistance | good |
Temperature resistance short term duration | 120 °C |
Humidity resistance | very good |
Static shear resistance at 23°C | good |
Adhesion to ABS (initial) | 12 N/cm |
Adhesion to ABS (after 14 days) | 13.5 N/cm |
Adhesion to PC (initial) | 14.5 N/cm |
Adhesion to PC (after 14 days) | 15.5 N/cm |
Adhesion to PET (initial) | 10 N/cm |
Adhesion to PET (after 14 days) | 10.5 N/cm |
Adhesion to PP (initial) | 8 N/cm |
Adhesion to PP (after 14 days) | 9.5 N/cm |
Adhesion to ABS (initial) | 12 N/cm |
Adhesion to ABS (after 14 days) | 13.5 N/cm |
Adhesion to PC (initial) | 14.5 N/cm |
Adhesion to PC (after 14 days) | 15.5 N/cm |
Adhesion to PET (initial) | 10 N/cm |
Adhesion to PET (after 14 days) | 10.5 N/cm |
Adhesion to PP (initial) | 8 N/cm |
Adhesion to PP (after 14 days) | 9.5 N/cm |