Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | white |
| Liner Type | glassine |
| Thickness of liner | 70 µm |
| Total thickness | 1150 µm |
| Weight of liner | 80 g/m² |
tesa® 4952
tesa® 4952 Double-sided PE Foam Tape (1150 µm)
Product Features
-
Versatile adhesive for high immediate adhesion on numerous substrates
- Fully outdoor suitable: UV, water and ageing resistant
- Compensates for differing thermal expansion of dissimilar materials
- High immediate bonding strength even at low bonding pressure
- Very good cold shock absorbtion
Product description
tesa® 4952 is a double-sided foam tape, frequently used for a wide range of different constructive mounting applications. The double-sided tape features a very good tack and excellent adhesiveness on smooth surfaces. The foam tape is resistant against UV-light, humidity, water, chemicals, and aging. The tape is ideal for indoor and outdoor usage, with a long-term temperature resistance of up to 80°C. tesa® 4952 is comprised of a high-quality, white closed-cell PE-foam backing, a shear-resistant modified acrylic adhesive, and a glassine lining. tesa® 4952 is especially suitable for fixing flat objects such as mirrors, signs, and decorative materials. Furthermore, the foam-tape acts as a good shock absorber, making it ideal for various sealing functions and for leveling out different thermal elongations of materials. tesa® 4952 has been externally certified for furniture mirror mounting.
Product details and specifications
Product Features
- Versatile adhesive for high immediate adhesion on numerous substrates
- Fully outdoor suitable: UV, water and ageing resistant
- Compensates for differing thermal expansion of dissimilar materials
- High immediate bonding strength even at low bonding pressure
- Very good cold shock absorbtion
Application Fields
1 Furniture mirror mounting
1 Mounting of car mirrors
1 Mounting functional trims & profiles
1 Mounting of decorative panel
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | white |
| Liner Type | glassine |
| Thickness of liner | 70 µm |
| Total thickness | 1150 µm |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Elongation at break | 200 % |
| Tensile strength | 10 N/cm |
| Chemical Resistance | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | good |
| Softener resistance | medium |
| Temperature resistance short term | 80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 80 °C |
| Tack | good |
Properties / Performance Values
| Elongation at break | 200 % |
| Tensile strength | 10 N/cm |
| Chemical Resistance | good |
| Humidity resistance | very good |
| Ageing resistance (UV) | good |
| Softener resistance | medium |
| Temperature resistance short term | 80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 80 °C |
| Tack | good |
Adhesion to Values
| Adhesion to ABS (initial) | 5 N/cm |
| Adhesion to ABS (after 14 days) | 8 N/cm |
| Adhesion to Aluminium (initial) | 5 N/cm |
| Adhesion to Aluminium (after 14 days) | 8 N/cm |
| Adhesion to PC (initial) | 5 N/cm |
| Adhesion to PC (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 2.8 N/cm |
| Adhesion to PET (initial) | 5 N/cm |
| Adhesion to PET (after 14 days) | 7 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.5 N/cm |
| Adhesion to PS (initial) | 5 N/cm |
| Adhesion to PS (after 14 days) | 7.5 N/cm |
| Adhesion to PVC (initial) | 5 N/cm |
| Adhesion to PVC (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 6.5 N/cm |
| Adhesion to Steel (after 14 days) | 8 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 5 N/cm |
| Adhesion to ABS (after 14 days) | 8 N/cm |
| Adhesion to Aluminium (initial) | 5 N/cm |
| Adhesion to Aluminium (after 14 days) | 8 N/cm |
| Adhesion to PC (initial) | 5 N/cm |
| Adhesion to PC (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 2.8 N/cm |
| Adhesion to PET (initial) | 5 N/cm |
| Adhesion to PET (after 14 days) | 7 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.5 N/cm |
| Adhesion to PS (initial) | 5 N/cm |
| Adhesion to PS (after 14 days) | 7.5 N/cm |
| Adhesion to PVC (initial) | 5 N/cm |
| Adhesion to PVC (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 6.5 N/cm |
| Adhesion to Steel (after 14 days) | 8 N/cm |
Additional Info
tesa® 4952 has been tested and approved by LGA institute for mirror mounting. Report number IWQ FSG 329 1189.
Peel Adhesion:
Peel Adhesion:
- immediately: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
- after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.