Product Construction
| Adhesive Type | modified acrylic |
| Backing material | PET film |
| Color | transparent |
| Color of liner | brown/blue logo |
| Liner Type | paper |
| Thickness of liner | 69 µm |
| Total thickness | 300 µm |
| Weight of liner | 80 g/m² |
tesa® 59651 - Team 4965 Thick
300µm double sided transparent PET film tape
Product Features
- tesa® 4965 Original in 300 µm
- High holding power at elevated temperatures
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
Product description
tesa® 59651 – Team 4965 Thick is a transparent, double-sided industrial mounting tape consisting of a PET backing and a tackified acrylic adhesive. The double-sided mounting tape is a thick version of tesa® 4965 Original and its adhesive is based on a patented and protected product technology. tesa® 59651 – Team 4965 Thick is used in various different industries for lamination and mounting applications, frequently for mounting bumper rails or bonding door elements. The double-sided industrial mounting tape is able to withstand numerous environmental factors such as humidity, UV light, and temperatures of up to 200°C for limited periods of time. The tackified acrylic adhesive offers excellent hold on various surfaces, high tack, and good shear strength.
Several products are equipped with this unique and high-performing product design. Together, these products make up Team 4965. This double-sided film tape assortment helps to easily select the most efficient tape based on customer demands, products, and processes. Explore the benefits of the full tesa® 4965 assortment here:
https://www.tesa.com/en/industry/general-applications/mounting/team-4965-assortment
Product details and specifications
Product Features
- tesa® 4965 Original in 300 µm
- High holding power at elevated temperatures
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
- Superior bonding strength, often also on low surface energy surfaces
- More bonding reliability for rougher substrates
- Low VOC – measured according to VDA 278 analysis
- Outstanding converting and die-cutting properties
Application Fields
- tesa® 59651 – Team 4965 Thick is used in various different industries for mounting and lamination applications
- Bumper-rail mounting
- Bonding door elements
Product Construction
| Adhesive Type | modified acrylic |
| Backing material | PET film |
| Color | transparent |
| Color of liner | brown/blue logo |
| Liner Type | paper |
| Thickness of liner | 69 µm |
| Total thickness | 300 µm |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Temperature resistance short term | 200 °C |
| Static shear resistance at 40°C | very good |
| Tack | good |
| Static shear resistance at 23°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance min. | -40 °C |
| Temperature resistance long term | 100 °C |
| Softener resistance | good |
| Humidity resistance | very good |
| Chemical Resistance | good |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Temperature resistance short term | 200 °C |
| Static shear resistance at 40°C | very good |
| Tack | good |
| Static shear resistance at 23°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance min. | -40 °C |
| Temperature resistance long term | 100 °C |
| Softener resistance | good |
| Humidity resistance | very good |
| Chemical Resistance | good |
Adhesion to Values
| Adhesion to ABS (initial) | 10.5 N/cm |
| Adhesion to ABS (after 14 days) | 11 N/cm |
| Adhesion to Aluminium (initial) | 9.3 N/cm |
| Adhesion to Aluminium (after 14 days) | 9.8 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14.3 N/cm |
| Adhesion to PE (initial) | 6 N/cm |
| Adhesion to PE (after 14 days) | 6.4 N/cm |
| Adhesion to PET (initial) | 7.7 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PS (initial) | 8.5 N/cm |
| Adhesion to PS (after 14 days) | 13.3 N/cm |
| Adhesion to PVC (initial) | 8.8 N/cm |
| Adhesion to PVC (after 14 days) | 14.7 N/cm |
| Adhesion to Steel (initial) | 13.8 N/cm |
| Adhesion to Steel (after 14 days) | 14.5 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 10.5 N/cm |
| Adhesion to ABS (after 14 days) | 11 N/cm |
| Adhesion to Aluminium (initial) | 9.3 N/cm |
| Adhesion to Aluminium (after 14 days) | 9.8 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14.3 N/cm |
| Adhesion to PE (initial) | 6 N/cm |
| Adhesion to PE (after 14 days) | 6.4 N/cm |
| Adhesion to PET (initial) | 7.7 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PS (initial) | 8.5 N/cm |
| Adhesion to PS (after 14 days) | 13.3 N/cm |
| Adhesion to PVC (initial) | 8.8 N/cm |
| Adhesion to PVC (after 14 days) | 14.7 N/cm |
| Adhesion to Steel (initial) | 13.8 N/cm |
| Adhesion to Steel (after 14 days) | 14.5 N/cm |
Additional Info
Low VOC – measured according to VDA 278 analysis, tesa® 59651 – Team 4965 Thick does not contain any single substances restricted by the drafted GB regulations (China).
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.