Product Construction
Adhesive Type | acrylic |
Backing material | PVC film |
Color | transparent |
Total thickness | 86 µm |
86µm double sided transparent PVC film tape without liner
tesa® 51903 is a transparent, double-sided adhesive tape without release liner featuring a PVC backing and an acrylic adhesive. The acrylic adhesive system of the double-sided linerless tape has different adhesion values on each side, which makes tesa® 51903 the perfect solution for box-closure applications. The different adhesion values on each side are precisely balanced, so that tesa® 51903 can be unwound easily, even after long periods of storage.
Adhesive Type | acrylic |
Backing material | PVC film |
Color | transparent |
Total thickness | 86 µm |
Adhesive Type | acrylic |
Backing material | PVC film |
Color | transparent |
Total thickness | 86 µm |
Elongation at break | 40 % |
Tensile strength | 35 N/cm |
Softener resistance | low |
Static shear resistance at 40°C | low |
Temperature resistance min. | -40 °C |
Static shear resistance at 23°C | low |
Chemical Resistance | medium |
Ageing resistance (UV) | very good |
Temperature resistance long term | 60 °C |
Tack | good |
Temperature resistance short term | 70 °C |
Humidity resistance | very good |
Elongation at break | 40 % |
Tensile strength | 35 N/cm |
Softener resistance | low |
Static shear resistance at 40°C | low |
Temperature resistance min. | -40 °C |
Static shear resistance at 23°C | low |
Chemical Resistance | medium |
Ageing resistance (UV) | very good |
Temperature resistance long term | 60 °C |
Tack | good |
Temperature resistance short term | 70 °C |
Humidity resistance | very good |
Adhesion to ABS (initial) | 2.8 N/cm |
Adhesion to ABS (after 14 days) | 2 N/cm |
Adhesion to Aluminium (initial) | 1.5 N/cm |
Adhesion to Aluminium (after 14 days) | 2.5 N/cm |
Adhesion to PC (initial) | 2.7 N/cm |
Adhesion to PC (after 14 days) | 1.8 N/cm |
Adhesion to PE (initial) | 1.2 N/cm |
Adhesion to PE (after 14 days) | 1.8 N/cm |
Adhesion to PET (initial) | 1.8 N/cm |
Adhesion to PET (after 14 days) | 2.2 N/cm |
Adhesion to PP (initial) | 1.7 N/cm |
Adhesion to PP (after 14 days) | 2.4 N/cm |
Adhesion to PS (initial) | 2.7 N/cm |
Adhesion to PS (after 14 days) | 2.7 N/cm |
Adhesion to PVC (initial) | 1.8 N/cm |
Adhesion to PVC (after 14 days) | 2.5 N/cm |
Adhesion to Steel (initial) | 2.4 N/cm |
Adhesion to Steel (after 14 days) | 3 N/cm |
Adhesion to ABS (initial) | 2.8 N/cm |
Adhesion to ABS (after 14 days) | 2 N/cm |
Adhesion to Aluminium (initial) | 1.5 N/cm |
Adhesion to Aluminium (after 14 days) | 2.5 N/cm |
Adhesion to PC (initial) | 2.7 N/cm |
Adhesion to PC (after 14 days) | 1.8 N/cm |
Adhesion to PE (initial) | 1.2 N/cm |
Adhesion to PE (after 14 days) | 1.8 N/cm |
Adhesion to PET (initial) | 1.8 N/cm |
Adhesion to PET (after 14 days) | 2.2 N/cm |
Adhesion to PP (initial) | 1.7 N/cm |
Adhesion to PP (after 14 days) | 2.4 N/cm |
Adhesion to PS (initial) | 2.7 N/cm |
Adhesion to PS (after 14 days) | 2.7 N/cm |
Adhesion to PVC (initial) | 1.8 N/cm |
Adhesion to PVC (after 14 days) | 2.5 N/cm |
Adhesion to Steel (initial) | 2.4 N/cm |
Adhesion to Steel (after 14 days) | 3 N/cm |