Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | black |
| Color of liner | brown/blue logo |
| Liner Type | paper |
| Thickness of liner | 69 µm |
| Total thickness | 205 µm |
| Weight of liner | 80 g/m² |
tesa® 59652 – Team 4965 Black
205µm double sided black PET film tape
Product Features
- tesa® 4965 Original in black with light-blocking properties
- Reliable bond, often also on low surface energy surfaces
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
Product description
tesa® 59652 – Team 4965 Black is a black, double-sided industrial mounting tape consisting of a PET backing and a tackified acrylic adhesive. The double-sided mounting tape is the black version of tesa® 4965 Original and its adhesive is based on a patented and protected product technology. The double-sided mounting tape with its opaque black backing helps to avoid undesired light exposure and contributes to light management in interior designs. tesa® 59652 – Team 4965 Black is able to withstand numerous environmental factors such as humidity, UV light, and temperatures of up to 200°C for limited periods of time. The tackified acrylic adhesive offers excellent hold on various surfaces, high tack, and good shear strength.
Several products are equipped with this unique and high-performing product design. Together, these products make up Team 4965. This double-sided film tape assortment helps to easily select the most efficient tape based on customer demands, products, and processes. Explore the benefits of the full tesa® 4965 assortment here:
https://www.tesa.com/en/industry/general-applications/mounting/team-4965-assortment
Product details and specifications
Product Features
- tesa® 4965 Original in black with light-blocking properties
- Reliable bond, often also on low surface energy surfaces
- Skin contact certification according to ISO 10993-5 and ISO 10993-10
- Immediate usability right after assembly
- Black color for automatic pick-and-place processes
- Low VOC – measured according to VDA 278 analysis
Application Fields
- tesa® 4965 – Team 4965 Black contributes to light management in interior designs
- LED-strip mounting
- Mounting lenses and cushioning foams in mobile phones
- Optical detection splicing
- Mounting exterior car mirrors in the automotive industry
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | black |
| Color of liner | brown/blue logo |
| Liner Type | paper |
| Thickness of liner | 69 µm |
| Total thickness | 205 µm |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Static shear resistance at 40°C | very good |
| Tack | good |
| Temperature resistance long term | 100 °C |
| Softener resistance | good |
| Temperature resistance min. | -40 °C |
| Chemical Resistance | good |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance short term | 200 °C |
Properties / Performance Values
| Elongation at break | 50 % |
| Tensile strength | 20 N/cm |
| Static shear resistance at 40°C | very good |
| Tack | good |
| Temperature resistance long term | 100 °C |
| Softener resistance | good |
| Temperature resistance min. | -40 °C |
| Chemical Resistance | good |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Ageing resistance (UV) | good |
| Temperature resistance short term | 200 °C |
Adhesion to Values
| Adhesion to ABS (initial) | 10.8 N/cm |
| Adhesion to ABS (after 14 days) | 11.9 N/cm |
| Adhesion to Aluminium (initial) | 10.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 12.6 N/cm |
| Adhesion to PC (initial) | 12.2 N/cm |
| Adhesion to PC (after 14 days) | 13.4 N/cm |
| Adhesion to PE (initial) | 5.6 N/cm |
| Adhesion to PE (after 14 days) | 6.6 N/cm |
| Adhesion to PET (initial) | 9.8 N/cm |
| Adhesion to PET (after 14 days) | 11.9 N/cm |
| Adhesion to PP (after 14 days) | 8.8 N/cm |
| Adhesion to PP (covered side, initial) | 6 N/cm |
| Adhesion to PS (initial) | 10.4 N/cm |
| Adhesion to PS (after 14 days) | 12.1 N/cm |
| Adhesion to PVC (initial) | 9.6 N/cm |
| Adhesion to PVC (after 14 days) | 12.8 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 14 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 10.8 N/cm |
| Adhesion to ABS (after 14 days) | 11.9 N/cm |
| Adhesion to Aluminium (initial) | 10.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 12.6 N/cm |
| Adhesion to PC (initial) | 12.2 N/cm |
| Adhesion to PC (after 14 days) | 13.4 N/cm |
| Adhesion to PE (initial) | 5.6 N/cm |
| Adhesion to PE (after 14 days) | 6.6 N/cm |
| Adhesion to PET (initial) | 9.8 N/cm |
| Adhesion to PET (after 14 days) | 11.9 N/cm |
| Adhesion to PP (after 14 days) | 8.8 N/cm |
| Adhesion to PP (covered side, initial) | 6 N/cm |
| Adhesion to PS (initial) | 10.4 N/cm |
| Adhesion to PS (after 14 days) | 12.1 N/cm |
| Adhesion to PVC (initial) | 9.6 N/cm |
| Adhesion to PVC (after 14 days) | 12.8 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 14 N/cm |
Additional Info
Low VOC – measured according to VDA 278 analysis, tesa® 59652 – Team 4965 Black does not contain any single substances restricted by the drafted GB regulations (China).
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.