Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | transparent |
| Color of liner | red |
| Liner Type | MOPP |
| Thickness of liner | 80 µm |
| Total thickness | 205 µm |
| Weight of liner | 72 g/m² |
tesa® 6190 Combitape Next Gen
205µm double sided filmic box sealing tape with fingerlift and integrated tear-tape
Sustainable Aspects
- tesa® 6190 Combitape Next Gen with -39% CO₂ emissions1 compared to tesa® 6190 Combitape
- Biomass balanced tackified acrylic adhesive
- 90% PCR PET in the backing
- Implementing closure and opening function in limited space
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
Product description
tesa® 6190 Combitape Next Gen is a transparent, double-sided mounting tape, produced with a biomass balanced adhesive and a 90% PCR PET backing which leads to a reduction in CO₂ emissions of -39%1 compared to tesa® 6190 Combitape. The double-sided filmic box sealing tape is supplied with fingerlift (extended liner) and integrated tear tape. tesa® 6190 Combitape Next Gen has been designed for corrugated-board cartons and is recycling friendly according to the INGEDE method. The biomass balanced tackified acrylic adhesive provides reliable bonding performance even at high temperatures and on rough cardboard surfaces.
Product details and specifications
Product Features
- Implementing closure and opening function in limited space
- Fast liner removal due to fingerlift
- High initial adhesion for fast closure
- Reliable bonding performance even at high temperatures and on rough corrugated-board surfaces
- Recycling friendly according to the INGEDE method
Application Fields
- tesa® 6190 Combitape Next Gen is especially designed for corrugated-board cartons
- Self-adhesive mail-order boxes
- Closing CD and book cartons
Sustainable Aspects
- tesa® 6190 Combitape Next Gen with -39% CO₂ emissions1 compared to tesa® 6190 Combitape
- Biomass balanced tackified acrylic adhesive
- 90% PCR PET in the backing
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | transparent |
| Color of liner | red |
| Liner Type | MOPP |
| Thickness of liner | 80 µm |
| Total thickness | 205 µm |
| Weight of liner | 72 g/m² |
Properties / Performance Values
| Elongation at break | 30 % |
| Tensile strength | 130 N/cm |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Temperature resistance short term | 200 °C |
| Ageing resistance (UV) | good |
| Tack | good |
| Temperature resistance long term | 100 °C |
| Chemical Resistance | good |
| Softener resistance | good |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | very good |
Properties / Performance Values
| Elongation at break | 30 % |
| Tensile strength | 130 N/cm |
| Humidity resistance | very good |
| Static shear resistance at 23°C | very good |
| Temperature resistance short term | 200 °C |
| Ageing resistance (UV) | good |
| Tack | good |
| Temperature resistance long term | 100 °C |
| Chemical Resistance | good |
| Softener resistance | good |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | very good |
Adhesion to Values
| Adhesion to ABS (initial) | 10.3 N/cm |
| Adhesion to ABS (after 14 days) | 12 N/cm |
| Adhesion to Aluminium (initial) | 9.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14 N/cm |
| Adhesion to PE (initial) | 5.8 N/cm |
| Adhesion to PE (after 14 days) | 6.9 N/cm |
| Adhesion to PET (initial) | 9.2 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PP (initial) | 6.8 N/cm |
| Adhesion to PP (after 14 days) | 7.9 N/cm |
| Adhesion to PS (initial) | 10.6 N/cm |
| Adhesion to PS (after 14 days) | 12 N/cm |
| Adhesion to PVC (initial) | 8.7 N/cm |
| Adhesion to PVC (after 14 days) | 13 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 11.8 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 10.3 N/cm |
| Adhesion to ABS (after 14 days) | 12 N/cm |
| Adhesion to Aluminium (initial) | 9.2 N/cm |
| Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
| Adhesion to PC (initial) | 12.6 N/cm |
| Adhesion to PC (after 14 days) | 14 N/cm |
| Adhesion to PE (initial) | 5.8 N/cm |
| Adhesion to PE (after 14 days) | 6.9 N/cm |
| Adhesion to PET (initial) | 9.2 N/cm |
| Adhesion to PET (after 14 days) | 9.5 N/cm |
| Adhesion to PP (initial) | 6.8 N/cm |
| Adhesion to PP (after 14 days) | 7.9 N/cm |
| Adhesion to PS (initial) | 10.6 N/cm |
| Adhesion to PS (after 14 days) | 12 N/cm |
| Adhesion to PVC (initial) | 8.7 N/cm |
| Adhesion to PVC (after 14 days) | 13 N/cm |
| Adhesion to Steel (initial) | 11.5 N/cm |
| Adhesion to Steel (after 14 days) | 11.8 N/cm |
Additional Info
1 Product Carbon Footprint (PCF) reduction for the new tesa® 6190 Combitape Next Gen (2000m x 23mm spool, PV0 red MOPP liner) compared to the current tesa® 6190 Combitape (2000m x 23mm spool, PV0 red MOPP liner) calculated in 2024 with Cradle-to-Gate values, including biogenic carbon uptake. The calculation of the CO₂ footprint was conducted in 2024, following the same approach as the ISO 14067-compliant comparative PCF study for tesa® 4965 Original Next Gen, available on tesa.com/4965-report. For detailed information on the tesa® 6190 Combitape Next Gen Product Carbon Footprint, please contact your local tesa sales representative.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads
Download the files below for more technical details and information on this product.