Product Construction
| Adhesive Type | low temperature activated reactive adhesive |
| Backing material | none |
| Color | black |
| Liner Type | PE-coated paper |
| Total thickness | 200 µm |
tesa® LTR 58488
200 µm black low temperature reactive HAF mounting tape
Product Features
- Extremely high bonding performance and reliability, even on slim bonding areas and thin design gaps
- Activated at low temperature and pressure
- Excellent shock resistance
Product description
tesa® Low Temperature Reactive (LTR) 58488 is a reactive mounting tape activated at moderate temperatures. This black double-sided tape has no backing. It is protected by a PE-coated paper liner.
It is activated by moderate heat and pressure applied during the assembly process.
Product details and specifications
Product Features
- Extremely high bonding performance and reliability, even on slim bonding areas and thin design gaps
- Activated at low temperature and pressure
- Excellent shock resistance
- Sebum resistant
- Very low oozing ratio
- At room temperature tesa® LTR 58488 is not tacky.
- tesa® LTR 58488 is free of halogen and compliant with current RoHS directive.
Application Fields
tesa® LTR 58488 is especially recommended for structural bonding of temperature sensitive substrates:
- Bonding of fabrics
- Bonding of plastics
- Mounting of sensitive electronic parts
Product Construction
| Adhesive Type | low temperature activated reactive adhesive |
| Backing material | none |
| Color | black |
| Liner Type | PE-coated paper |
| Total thickness | 200 µm |
Properties / Performance Values
| Low VOC | very good |
| Bonding strength (push-out) | 7.5 N/mm² |
Properties / Performance Values
| Low VOC | very good |
| Bonding strength (push-out) | 7.5 N/mm² |
Additional Info
Technical recommendations:
tesa® LTR 58488 is not self adhesive. It is activated by heat and pressure over a certain interval. The following values are recommendations for bond line parameters to start with.
1. Pre-lamination:
During pre-lamination, laminate the adhesive tape onto the first component.
Setting:
2. Bonding:
Remove the liner from tape after the pre-lamination step.
Position the second component. Apply temperature and pressure for the bonding time to reach sufficient bonding strength.
Setting:
Short cycle times can be achieved at 110 °C bond line temperature. For activation at lower temperatures, increase the heat-press time or combine a short heat-press step with oven curing.
To reach maximum bonding strength, surfaces should be clean and dry. Allow at least 1-2 hours dwell-time after bonding before performance testing. Final bonding strength will be reached after 24 hours.
Bonding strength values were obtained under standard laboratory conditions (Material: PC/PC; bonding conditions: temperature (jig) = 90 °C; pressure = 5 bar; time = 120 sec).
Storage:
tesa recommends storage in original packaging in cool and dry conditions.
Low Temperature Reactive should not be exposed to more than 35 °C before bonding (during transport, storage and converting).
The shelf life is 15 months after coating date. For the actual shelf life please refer to the best before date on the label in the log roll core.
¹ ‘Pre-lamination’ and ‘Bonding’ temperature refer to the data that is measured in the bond line.
² ‘Pre-lamination’ and ‘Bonding’ pressure refer to the force that is transferred from jig surface directly to the bonding area.
tesa® LTR 58488 is not self adhesive. It is activated by heat and pressure over a certain interval. The following values are recommendations for bond line parameters to start with.
1. Pre-lamination:
During pre-lamination, laminate the adhesive tape onto the first component.
Setting:
- Temperature¹: 50–60 °C
- Pressure²: 1–3 bar
- Time: 5–20 s
2. Bonding:
Remove the liner from tape after the pre-lamination step.
Position the second component. Apply temperature and pressure for the bonding time to reach sufficient bonding strength.
Setting:
- Temperature¹: 75–110 °C
- Pressure²: 2–4 bar
- Time: 10–480 s
Short cycle times can be achieved at 110 °C bond line temperature. For activation at lower temperatures, increase the heat-press time or combine a short heat-press step with oven curing.
To reach maximum bonding strength, surfaces should be clean and dry. Allow at least 1-2 hours dwell-time after bonding before performance testing. Final bonding strength will be reached after 24 hours.
Bonding strength values were obtained under standard laboratory conditions (Material: PC/PC; bonding conditions: temperature (jig) = 90 °C; pressure = 5 bar; time = 120 sec).
Storage:
tesa recommends storage in original packaging in cool and dry conditions.
Low Temperature Reactive should not be exposed to more than 35 °C before bonding (during transport, storage and converting).
The shelf life is 15 months after coating date. For the actual shelf life please refer to the best before date on the label in the log roll core.
¹ ‘Pre-lamination’ and ‘Bonding’ temperature refer to the data that is measured in the bond line.
² ‘Pre-lamination’ and ‘Bonding’ pressure refer to the force that is transferred from jig surface directly to the bonding area.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads
Download the files below for more technical details and information on this product.
![[en-en] tesa_HAF-black_dr_001](/en/files/images/202402/0/medium-11173881,11173881_padded1x1_18.webp "tesa_HAF-black_dr_001")
![[en-en] tesa_HAF-amber_dr_001](/en/files/images/202402/0/medium-11173882,11173882_padded1x1_18.webp "tesa_HAF-amber_dr_001")