tesa® LTT 8741

30 µm Low Temperature Thermoplastic Structural Bonding Film


Product description

tesa® Low Temperature Thermoplast (LTT) 8741 is a non-reactive sturctural bonding film activated at moderate temperatures. This translucent film has no backing. It is protected by a dark-grey PE liner. tesa® LTT 8741 is free of halogen and compliant with current RoHS directive. At room temperature tesa® LTT 8741 is not tacky. It is activated by moderate heat and pressure applied during the assembly process.
Main features

  • High peel adhesion on wide variety of fabrics
  • Low pre-lamination temperature starting from 60 °C
  • No yellowing
  • Good re-workability from smooth substrates


Product details and specifications

Application Fields

tesa® LTT 8741 is especially recommended for bonding of fabrics to various substrates.
Adhesion properties:
Peel adhesion to polyester fabric: 7 N/cm
Technical recommendations:
tesa® LTT 8741 is not self-adhesive. It is activated by heat and pressure over a certain interval. The following values are recommendations for bond line parameters to start with.
1) Pre-lamination
During pre-lamination, laminate the film onto the first component.
Setting:
  • Temperature¹: 60–90 °C
  • Pressure²: 1–5 bar
  • Time: 5–20 s
2) Bonding
Remove the liner from the film after the pre-lamination step. Position the second component. Apply temperature and pressure for the bonding time to reach sufficient bonding strength.
Setting:
  • Temperature¹: 80–120 °C
  • Pressure²: 1–5 bar
  • Time: 10–480 s
Temperature, pressure and time will depend upon the type and thickness of the substrates. Generally, thicker substrates or lower bonding temperatures will require longer bonding times.
Short cycle times can be achieved at 110 °C bond line temperature. For activation at lower temperatures, increase the heat-press time or combine a short heat-press step with oven curing.
Peel adhesion values were obtained under standard laboratory conditions (reinforcement backing 23 µm PET; bonding conditions: temperature = 90 °C; pressure = 5 bar; time = 120 sec).
To reach maximum bonding strength, surfaces should be clean and dry. Allow at least 1-2 hours dwell-time after bonding before performance testing. Final bonding strength will be reached after 24 hours.

¹ ‘Pre-lamination’ and ‘Bonding’ temperature refer to the data that is measured in the bond line. ² ‘Pre-lamination’ and ‘Bonding’ pressure refer to the force that is transferred from jig surface directly to the bonding area.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads

Download the files below for more technical details and information on this product.

Get in contact with us!

Contact us

How can we help you? How can we get in touch? In accordance to our Privacy Policy your data will only be stored in a manner appropriate to the nature of the request to fulfill your needs.

Thank you for your message

We'll get back to you as soon as possible.

 

Best regards

Your tesa Team

Something went wrong. Please try again later.