Product Construction
Adhesive Type | tackified acrylic |
Backing material | PET |
Adhesive Type | tackified acrylic |
Backing material | PET |
Adhesive Type | tackified acrylic |
Backing material | PET |
Elongation at break | 50 % |
Tensile strength | 30 N/cm |
Static shear resistance at 23°C | very good |
Optical density | 3.7 |
Dielectric breakdown voltage | 4000 V |
Static shear resistance at 40°C | very good |
Temperature resistance short term | 200 °C |
Temperature resistance long term | 100 °C |
Humidity resistance | good |
Ageing resistance (UV) | very good |
Softener resistance | very good |
Elongation at break | 50 % |
Tensile strength | 30 N/cm |
Static shear resistance at 23°C | very good |
Optical density | 3.7 |
Dielectric breakdown voltage | 4000 V |
Static shear resistance at 40°C | very good |
Temperature resistance short term | 200 °C |
Temperature resistance long term | 100 °C |
Humidity resistance | good |
Ageing resistance (UV) | very good |
Softener resistance | very good |
Adhesion to ABS (initial) | 3.9 N/cm |
Adhesion to ABS (after 14 days) | 4.7 N/cm |
Adhesion to Aluminium (initial) | 3.8 N/cm |
Adhesion to Aluminium (after 14 days) | 5.3 N/cm |
Adhesion to Glass (initial) | 4.3 N/cm |
Adhesion to Glass (after 14 days) | 4.9 N/cm |
Adhesion to PC (initial) | 3.9 N/cm |
Adhesion to PC (after 14 days) | 5.2 N/cm |
Adhesion to Steel (initial) | 4.2 N/cm |
Adhesion to Steel (after 14 days) | 5.3 N/cm |
Adhesion to ABS (initial) | 3.9 N/cm |
Adhesion to ABS (after 14 days) | 4.7 N/cm |
Adhesion to Aluminium (initial) | 3.8 N/cm |
Adhesion to Aluminium (after 14 days) | 5.3 N/cm |
Adhesion to Glass (initial) | 4.3 N/cm |
Adhesion to Glass (after 14 days) | 4.9 N/cm |
Adhesion to PC (initial) | 3.9 N/cm |
Adhesion to PC (after 14 days) | 5.2 N/cm |
Adhesion to Steel (initial) | 4.2 N/cm |
Adhesion to Steel (after 14 days) | 5.3 N/cm |