Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET |
| Color | transparent |
| Color of liner | brown/blue logo |
| Liner Type | glassine |
| Thickness of liner | 69 µm |
| Total thickness | 100 µm |
tesa® 58334 100µm D/S PET
tesa® 58334 is a 100µm differentiated double-sided transparent PET tape equipped with tackified acrylic adhesive.
Product Features
- Very fast wetting performance on rough surface, such as mica plate (>1.2N/cm)
- Outstanding conformability
- Excellent initial peel strength
Product description
The tackified acrylic adhesive offers outstanding initial peel strength on polar substrate and fit to rough surface such as mica plate. Its PET backing ensures excellent converting performance. The glassine liner ensures it can be easily released without adhesive residue during application.
Product details and specifications
Product Features
- Very fast wetting performance on rough surface, such as mica plate (>1.2N/cm)
- Outstanding conformability
- Excellent initial peel strength
- Good handling performance in converting process
- Good resistance to demanding automotive environmental conditions
Application Fields
tesa® 58334 has especially been developed for power battery demanding mounting, lamination and converting application with excellent wetting performance on its open side.
Mounting in power battery or lamination application such as:
Mounting in power battery or lamination application such as:
- Mica mounting
- Aerogel mounting
- other demanding mounting
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET |
| Color | transparent |
| Color of liner | brown/blue logo |
| Liner Type | glassine |
| Thickness of liner | 69 µm |
| Total thickness | 100 µm |
Properties / Performance Values
| Tack | very good |
| Temperature resistance long term | 125 °C |
| Humidity resistance | good |
| Static shear resistance at 23°C | good |
| Dielectric breakdown voltage | 5900 V |
Properties / Performance Values
| Tack | very good |
| Temperature resistance long term | 125 °C |
| Humidity resistance | good |
| Static shear resistance at 23°C | good |
| Dielectric breakdown voltage | 5900 V |
Adhesion to Values
| Adhesion to Aluminium (initial) | 5.6 N/cm |
| Adhesion to Aluminium (after 14 days) | 9.5 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 9.7 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.4 N/cm |
| Adhesion to Steel (covered side, initial) | 6.1 N/cm |
Adhesion to Values
| Adhesion to Aluminium (initial) | 5.6 N/cm |
| Adhesion to Aluminium (after 14 days) | 9.5 N/cm |
| Adhesion to Steel (initial) | 7 N/cm |
| Adhesion to Steel (after 14 days) | 9.7 N/cm |
| Adhesion to Steel (covered side, after 14 days) | 9.4 N/cm |
| Adhesion to Steel (covered side, initial) | 6.1 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.