Product Construction
Adhesive Type | tackified acrylic |
Backing material | PET |
Color | transparent |
Color of liner | white with tesa logo |
Liner Type | glassine |
Thickness of liner | 69 µm |
Total thickness | 100 µm |
tesa® 58374
is a transparent 100µm double-sided flame retardant PET tape. This tape has especially been developed for power battery demanding mounting, lamination and converting application with flame retardant property as an added value. Due to its non-flammable property it is particularly designed to meet power battery automobile requirement.
Mounting in power battery olamination application required additional flame retardant property.
Adhesive Type | tackified acrylic |
Backing material | PET |
Color | transparent |
Color of liner | white with tesa logo |
Liner Type | glassine |
Thickness of liner | 69 µm |
Total thickness | 100 µm |
Adhesive Type | tackified acrylic |
Backing material | PET |
Color | transparent |
Color of liner | white with tesa logo |
Liner Type | glassine |
Thickness of liner | 69 µm |
Total thickness | 100 µm |
Temperature resistance long term | 125 °C |
Temperature resistance short term | 200 °C |
Static shear resistance at 23°C | good |
Dielectric breakdown voltage | 6000 V |
Temperature resistance long term | 125 °C |
Temperature resistance short term | 200 °C |
Static shear resistance at 23°C | good |
Dielectric breakdown voltage | 6000 V |
Adhesion to Aluminium (initial) | 7.3 N/cm |
Adhesion to Glass (initial) | 6.5 N/cm |
Adhesion to Glass (covered side, initial) | 7.4 N/cm |
Adhesion to PET (initial) | 8.5 N/cm |
Adhesion to Steel (initial) | 8.2 N/cm |
Adhesion to Steel (after 14 days) | 9.5 N/cm |
Adhesion to Aluminium (initial) | 7.3 N/cm |
Adhesion to Glass (initial) | 6.5 N/cm |
Adhesion to Glass (covered side, initial) | 7.4 N/cm |
Adhesion to PET (initial) | 8.5 N/cm |
Adhesion to Steel (initial) | 8.2 N/cm |
Adhesion to Steel (after 14 days) | 9.5 N/cm |