Product Construction
Backing | none |
Color | transparent |
Color of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Total thickness | _NULL µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
220 µm reinforced water-based acrylic adhesive layer with PET scrim for mounting applications in automotive interiors
tesa® 66022 is a conformable, water-based acrylic adhesive tape with a thickness of 220 µm, reinforced by a PET scrim. This tape has especially been developed for all kinds of demanding lamination and mounting applications. Due to its low VOC property it is particularly designed to meet automotive interior requirements.
tesa® 66022 is suitable for laminating all kinds of foam, fleece, and felt substrates and mounting light interior components.
Backing | none |
Color | transparent |
Color of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Total thickness | _NULL µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
Backing | none |
Color | transparent |
Color of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Total thickness | _NULL µm |
Type of adhesive | type: water-based acrylic |
Type of liner | type: glassine |
Suitable for die cutting | yes |
Fogging | very good |
Suitable for rough surfaces | very good |
Temperature resistance max. | 200 °C |
Low VOC | very good |
Temperature resistance min. | -40 °C |
Tack | very good |
Suitable for die cutting | yes |
Fogging | very good |
Suitable for rough surfaces | very good |
Temperature resistance max. | 200 °C |
Low VOC | very good |
Temperature resistance min. | -40 °C |
Tack | very good |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 3 days) | 18 N/cm |
Adhesion to PC (initial) | 19.1 N/cm |
Adhesion to PC (after 3 days) | 19.4 N/cm |
Adhesion to PE (initial) | 9.2 N/cm |
Adhesion to PE (after 3 days) | 9 N/cm |
Adhesion to PET (initial) | 16.2 N/cm |
Adhesion to PET (after 3 days) | 18.1 N/cm |
Adhesion to PET fleece Headliner A (after 3 days) | 8 N/cm |
Adhesion to PET fleece Headliner A (initial) | 6 N/cm |
Adhesion to PP (initial) | 14 N/cm |
Adhesion to PP (after 3 days) | 16 N/cm |
Adhesion to PS (initial) | 17.7 N/cm |
Adhesion to PS (after 3 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 19.3 N/cm |
Adhesion to Steel (initial) | 12.3 N/cm |
Adhesion to Steel (after 3 days) | 17.3 N/cm |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 3 days) | 18 N/cm |
Adhesion to PC (initial) | 19.1 N/cm |
Adhesion to PC (after 3 days) | 19.4 N/cm |
Adhesion to PE (initial) | 9.2 N/cm |
Adhesion to PE (after 3 days) | 9 N/cm |
Adhesion to PET (initial) | 16.2 N/cm |
Adhesion to PET (after 3 days) | 18.1 N/cm |
Adhesion to PET fleece Headliner A (after 3 days) | 8 N/cm |
Adhesion to PET fleece Headliner A (initial) | 6 N/cm |
Adhesion to PP (initial) | 14 N/cm |
Adhesion to PP (after 3 days) | 16 N/cm |
Adhesion to PS (initial) | 17.7 N/cm |
Adhesion to PS (after 3 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 19.3 N/cm |
Adhesion to Steel (initial) | 12.3 N/cm |
Adhesion to Steel (after 3 days) | 17.3 N/cm |
Download the files below for more technical details and information on this product.