Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | non-woven |
| Color | translucent |
| Liner Type | PE-coated paper |
| Thickness of liner | 125 µm |
| Total thickness | 130 µm |
tesa® 66893
tesa® 66893 LOW VOC & LOW ODOR 130µm D/S NW Tape
Product description
- Low VOC – very low level of total VOC (volatile organic compounds) values
- Low odor – no unpleasant and pungent odor
- Excellent bonding strength to a wide variety of substrates
- New liner pattern design with green color printing
Product details and specifications
Application Fields
Focus on indoor mounting applications which customers have high standards for harmful chemical substances and odor.
- Control panel mounting
- Decorative layer lamination
- Component mounting
- Screw hole covering lamination
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | non-woven |
| Color | translucent |
| Liner Type | PE-coated paper |
| Thickness of liner | 125 µm |
| Total thickness | 130 µm |
Properties / Performance Values
| Elongation at break | 5 % |
| Tensile strength | 13 N/cm |
| Static shear resistance at 23°C | very good |
| Static shear resistance at 70°C | very good |
| Temperature resistance short term | 130 °C |
| Static shear resistance at 40°C | very good |
Properties / Performance Values
| Elongation at break | 5 % |
| Tensile strength | 13 N/cm |
| Static shear resistance at 23°C | very good |
| Static shear resistance at 70°C | very good |
| Temperature resistance short term | 130 °C |
| Static shear resistance at 40°C | very good |
Adhesion to Values
| Adhesion to ABS (initial) | 9 N/cm |
| Adhesion to ABS (after 3 days) | 15 N/cm |
| Adhesion to ASTM (initial) | 14 N/cm |
| Adhesion to Glass (initial) | 16 N/cm |
| Adhesion to Glass (after 3 days) | 16 N/cm |
| Adhesion to PC (initial) | 10 N/cm |
| Adhesion to PC (after 3 days) | 13 N/cm |
| Adhesion to PP (initial) | 3.5 N/cm |
| Adhesion to PP (after 3 days) | 5 N/cm |
| Adhesion to PVC (initial) | 9.5 N/cm |
| Adhesion to Steel (initial) | 14 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 9 N/cm |
| Adhesion to ABS (after 3 days) | 15 N/cm |
| Adhesion to ASTM (initial) | 14 N/cm |
| Adhesion to Glass (initial) | 16 N/cm |
| Adhesion to Glass (after 3 days) | 16 N/cm |
| Adhesion to PC (initial) | 10 N/cm |
| Adhesion to PC (after 3 days) | 13 N/cm |
| Adhesion to PP (initial) | 3.5 N/cm |
| Adhesion to PP (after 3 days) | 5 N/cm |
| Adhesion to PVC (initial) | 9.5 N/cm |
| Adhesion to Steel (initial) | 14 N/cm |
Additional Info
The low VOC is tested according to China passenger vehicle manufactory Ford odor test method.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.