Product Construction
| Backing material | PE foam |
| Color | white |
| Colour of liner | brown |
| Thickness of liner | 70 µm |
| Total thickness | 1150 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | glassine |
| Weight of liner | 80 g/m² |
tesa® 4952
Double-sided PE-foam mounting tape
Product description
tesa® 4952 is a double sided PE foam tape, consisting of a highly conformable closed cell PE-foam backing and a tackified acrylic adhesive. The foam tape offers a highly versatile adhesive for high immediate adhesion on numerous types of substrates and high immediate bonding strength even at low bonding pressure. tesa® 4952 features excellent resistance to water, UV and ageing, making it completely suitable for outdoors. The double sided foam tape is capable of compensating different thermal expansions of different materials. tesa® 4952 features very good cold shock absorption. tesa® 4952 is ideally used for constructive mounting applications and has been externally certified for mirror mounting.
tesa® 4952 has been externally tested and certified for mirror mounting by the LGA institute. Report number IWQ FSG 329 1189. The tape has an immediate peel adhesion: foam splitting on steel, aluminium, ABS, PC, PS, PET, PVC. And a peel adhesion after 14 days: foam splitting on steel, aluminium, ABS, PC, PS, PET, PVC.
Product details and specifications
Application Fields
- tesa® 4952 is used for constructive mounting applications
- The foam tape is used for furniture mirror mounting
- The double sided tape is used for the mounting of car mirrors
- tesa® 4952 is used for mounting functional trims & profiles
- tesa® 4952 is used for the mounting of decorative panels in the interior fitout industry
Product Construction
| Backing material | PE foam |
| Color | white |
| Colour of liner | brown |
| Thickness of liner | 70 µm |
| Total thickness | 1150 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | glassine |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Elongation at break | 200 % |
| Tensile strength | 10 N/cm |
| Softener resistance | medium |
| Temperature resistance short term | 80 °C |
| Tack | good |
| Static shear resistance at 23°C | good |
| Humidity resistance | very good |
| Temperature resistance long term | 80 °C |
| Chemical resistance | good |
| Static shear resistance at 40°C | good |
| Ageing resistance (UV) | good |
Properties / Performance Values
| Elongation at break | 200 % |
| Tensile strength | 10 N/cm |
| Softener resistance | medium |
| Temperature resistance short term | 80 °C |
| Tack | good |
| Static shear resistance at 23°C | good |
| Humidity resistance | very good |
| Temperature resistance long term | 80 °C |
| Chemical resistance | good |
| Static shear resistance at 40°C | good |
| Ageing resistance (UV) | good |
Adhesion to Values
| Adhesion to ABS (initial) | 5 N/cm |
| Adhesion to ABS (after 14 days) | 8 N/cm |
| Adhesion to Aluminium (initial) | 5 N/cm |
| Adhesion to Aluminium (after 14 days) | 8 N/cm |
| Adhesion to PC (initial) | 5 N/cm |
| Adhesion to PC (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 2.8 N/cm |
| Adhesion to PET (initial) | 5 N/cm |
| Adhesion to PET (after 14 days) | 7 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.5 N/cm |
| Adhesion to PS (initial) | 5 N/cm |
| Adhesion to PS (after 14 days) | 7.5 N/cm |
| Adhesion to PVC (initial) | 5 N/cm |
| Adhesion to PVC (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 6.5 N/cm |
| Adhesion to Steel (after 14 days) | 8 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 5 N/cm |
| Adhesion to ABS (after 14 days) | 8 N/cm |
| Adhesion to Aluminium (initial) | 5 N/cm |
| Adhesion to Aluminium (after 14 days) | 8 N/cm |
| Adhesion to PC (initial) | 5 N/cm |
| Adhesion to PC (after 14 days) | 8 N/cm |
| Adhesion to PE (initial) | 2.7 N/cm |
| Adhesion to PE (after 14 days) | 2.8 N/cm |
| Adhesion to PET (initial) | 5 N/cm |
| Adhesion to PET (after 14 days) | 7 N/cm |
| Adhesion to PP (initial) | 2.8 N/cm |
| Adhesion to PP (after 14 days) | 5.5 N/cm |
| Adhesion to PS (initial) | 5 N/cm |
| Adhesion to PS (after 14 days) | 7.5 N/cm |
| Adhesion to PVC (initial) | 5 N/cm |
| Adhesion to PVC (after 14 days) | 8 N/cm |
| Adhesion to Steel (initial) | 6.5 N/cm |
| Adhesion to Steel (after 14 days) | 8 N/cm |
Additional Info
tesa® 4952 has been tested and approved by LGA institute for mirror mounting. Report number IWQ FSG 329 1189.
Peel Adhesion:
- immediately: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
- after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
Peel Adhesion:
- immediately: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
- after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.