Product Construction
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 3000 µm |
| Type of adhesive | tackified acrylic |
tesa® 62530
Double sided PE-foam mounting tape
Product description
tesa® 62530 is a double sided PE foam tape for general mounting applications. It consists of a highly conformable closed cell PE foam backing and a tackified acrylic adhesive. The foam tape features good adhesion on strongly structured surfaces as well as a high tack and a short dwell time until reaching final adhesion. tesa® 62530 is able to withstand humidity, chemicals, softeners and UV light.
tesa® 62530 is a highly versatile adhesive, offering excellent immediate adhesion on numerous substrates, even at low bonding pressures. The double sided foam tape is fully suitable for outdoor use, featuring water-, ageing- and UV-resistance. The acrylic foam offers very good cold shock absorption, is capable of levelling out different thermal expansions and offers excellent bonding strength. Due to the foam’s conformability, tesa® 62530 has a strong hold even on irregular or rough substrates.
Product details and specifications
Application Fields
- tesa® 62530 is used for demanding long-term constructive applications, including:
- Window skirting trims
- Muntin bars
- Dust and moisture seals
- Decorative elements on doors
- The foam tape is available with other liner variants
- tesa® 62530 is available in various thicknesses: 500 µm, 800µm, 1,600 µm, 2,000 µm and 3,000 µm
Product Construction
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 3000 µm |
| Type of adhesive | tackified acrylic |
Properties / Performance Values
| Elongation at break | 160 % |
| Tensile strength | 13.3 N/cm |
| Batteries required | no |
| Ageing resistance (UV) | good |
| Tensibility | 140 % |
| Tack | good |
| Chemical resistance | very good |
| Humidity resistance | very good |
| Softener resistance | medium |
| Temperature resistance long term | 80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 80 °C |
Properties / Performance Values
| Elongation at break | 160 % |
| Tensile strength | 13.3 N/cm |
| Batteries required | no |
| Ageing resistance (UV) | good |
| Tensibility | 140 % |
| Tack | good |
| Chemical resistance | very good |
| Humidity resistance | very good |
| Softener resistance | medium |
| Temperature resistance long term | 80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 80 °C |
Adhesion to Values
| Adhesion to ABS (initial) | 6 N/cm |
| Adhesion to ABS (after 14 days) | 6 N/cm |
| Adhesion to Aluminium (initial) | 6 N/cm |
| Adhesion to Aluminium (after 14 days) | 6 N/cm |
| Adhesion to PC (initial) | 6 N/cm |
| Adhesion to PC (after 14 days) | 6 N/cm |
| Adhesion to PE (initial) | 2 N/cm |
| Adhesion to PE (after 14 days) | 2 N/cm |
| Adhesion to PET (initial) | 6 N/cm |
| Adhesion to PET (after 14 days) | 6 N/cm |
| Adhesion to PP (initial) | 6 N/cm |
| Adhesion to PP (after 14 days) | 6 N/cm |
| Adhesion to PS (initial) | 6 N/cm |
| Adhesion to PS (after 14 days) | 6 N/cm |
| Adhesion to PVC (initial) | 6 N/cm |
| Adhesion to PVC (after 14 days) | 6 N/cm |
| Adhesion to Steel (initial) | 6 N/cm |
| Adhesion to Steel (after 14 days) | 6 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 6 N/cm |
| Adhesion to ABS (after 14 days) | 6 N/cm |
| Adhesion to Aluminium (initial) | 6 N/cm |
| Adhesion to Aluminium (after 14 days) | 6 N/cm |
| Adhesion to PC (initial) | 6 N/cm |
| Adhesion to PC (after 14 days) | 6 N/cm |
| Adhesion to PE (initial) | 2 N/cm |
| Adhesion to PE (after 14 days) | 2 N/cm |
| Adhesion to PET (initial) | 6 N/cm |
| Adhesion to PET (after 14 days) | 6 N/cm |
| Adhesion to PP (initial) | 6 N/cm |
| Adhesion to PP (after 14 days) | 6 N/cm |
| Adhesion to PS (initial) | 6 N/cm |
| Adhesion to PS (after 14 days) | 6 N/cm |
| Adhesion to PVC (initial) | 6 N/cm |
| Adhesion to PVC (after 14 days) | 6 N/cm |
| Adhesion to Steel (initial) | 6 N/cm |
| Adhesion to Steel (after 14 days) | 6 N/cm |
Additional Info
Peel Adhesion:
- Immediate and after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
Longterm dampening properties and temperature resistance have been certified by ift institute, Germany (Report no. 105 32948/1)
- Immediate and after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
Longterm dampening properties and temperature resistance have been certified by ift institute, Germany (Report no. 105 32948/1)
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.