Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 31.5 mils
800 µm |
tesa® 62508
800µm/31.5 mils double sided PE foam tape
Product description
tesa® 62508 is a double sided PE foam tape for mounting applications. It consists of a highly conformable PE foam backing and a tackified acrylic adhesive.
Product benefits:
- High ultimate adhesion level for a reliable bonding performance
- Fully outdoor suitable: UV, water and ageing resistant
- Conformable PE foam core with high inner strength
- Suitable for automatic and manual module assembly
- Easy solar module assembly due to a high foam compression rate
Product details and specifications
Application Fields
- Solar module frames
- Mounting of trims and profiles
- General mounting applications
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 31.5 mils
800 µm |
Properties / Performance Values
| Elongation at break | 190 % |
| Tensile strength | 5.42 lbs/in
9.5 N/cm |
| Humidity resistance | very good |
| Temperature resistance short term | 176 °F
80 °C |
| Softener resistance | medium |
| Ageing resistance (UV) | very good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 176 °F
80 °C |
| Tack | good |
| Static shear resistance at 40°C | good |
Properties / Performance Values
| Elongation at break | 190 % |
| Tensile strength | 5.42 lbs/in
9.5 N/cm |
| Humidity resistance | very good |
| Temperature resistance short term | 176 °F
80 °C |
| Softener resistance | medium |
| Ageing resistance (UV) | very good |
| Static shear resistance at 23°C | good |
| Temperature resistance long term | 176 °F
80 °C |
| Tack | good |
| Static shear resistance at 40°C | good |
Adhesion to Values
| Adhesion to ABS (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to ABS (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Aluminium (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to Aluminium (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PC (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to PC (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PE (initial) | 0.51 lbs/in
0.9 N/cm |
| Adhesion to PE (after 14 days) | 0.51 lbs/in
0.9 N/cm |
| Adhesion to PET (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PET (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PP (initial) | 0.69 lbs/in
1.2 N/cm |
| Adhesion to PP (covered side, after 14 days) | 0.69 lbs/in
1.2 N/cm |
| Adhesion to PVC (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to PVC (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Steel (initial) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Steel (after 14 days) | 7.71 lbs/in
13.5 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to ABS (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Aluminium (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to Aluminium (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PC (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to PC (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PE (initial) | 0.51 lbs/in
0.9 N/cm |
| Adhesion to PE (after 14 days) | 0.51 lbs/in
0.9 N/cm |
| Adhesion to PET (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PET (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to PP (initial) | 0.69 lbs/in
1.2 N/cm |
| Adhesion to PP (covered side, after 14 days) | 0.69 lbs/in
1.2 N/cm |
| Adhesion to PVC (initial) | 4.57 lbs/in
8 N/cm |
| Adhesion to PVC (after 14 days) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Steel (initial) | 7.71 lbs/in
13.5 N/cm |
| Adhesion to Steel (after 14 days) | 7.71 lbs/in
13.5 N/cm |
Additional Info
Liner variants:
Peel Adhesion:
tesa® 62508 is recognized by UL as photovoltaic polymeric material (QIHE2).
tesa® 62508 has been tested by TÜV Rheinland, Germany. The test confirms the longterm adhesion performance after IEC 61215 climate tests and a 85°C/185°F temperature resistance.
The temperature resistance (short/long) of tesa® 62508 has been approved according to tesa test method under static load.
- PV0 brown glassine paper (71 µm/2.8 mils)
- PV13 transparent PET film (50 µm/2 mils)
- PV15 blue PE film (100 µm/3.9 mils)
Peel Adhesion:
- immediately: foam splitting on steel
- after 14 days: foam splitting on steel, ABS, Aluminium, PC, PET, PS, PVC
tesa® 62508 is recognized by UL as photovoltaic polymeric material (QIHE2).
tesa® 62508 has been tested by TÜV Rheinland, Germany. The test confirms the longterm adhesion performance after IEC 61215 climate tests and a 85°C/185°F temperature resistance.
The temperature resistance (short/long) of tesa® 62508 has been approved according to tesa test method under static load.
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.