Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 118.11 mils
3000 µm |
tesa® 62530
3000 µm/118.11 mils double sided PE foam tape
Product description
tesa® 62530 is a double sided PE foam tape for general mounting applications. It consists of a highly conformable closed cell PE foam backing and a tackified acrylic adhesive.
Product benefits:
- Good adhesion on strongly structured surfaces
- Versatile adhesive for high immediate adhesion on numerous substrates
- Fully outdoor suitable: UV, water and ageing resistant
- High immediate adhesion even at low bonding pressure
- Very good cold shock absorption
Product details and specifications
Application Fields
- Window skirting trims
- Muntin bars
- Dust and moisture seals
- Decorative elements on doors
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PE foam |
| Color | black/white |
| Total thickness | 118.11 mils
3000 µm |
Properties / Performance Values
| Elongation at break | 160 % |
| Tensile strength | 7.59 lbs/in
13.3 N/cm |
| Batteries required | no |
| Ageing resistance (UV) | good |
| Tensibility | 140 % |
| Tack | good |
| Chemical Resistance | very good |
| Humidity resistance | very good |
| Softener resistance | medium |
| Temperature resistance long term | 176 °F
80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 176 °F
80 °C |
Properties / Performance Values
| Elongation at break | 160 % |
| Tensile strength | 7.59 lbs/in
13.3 N/cm |
| Batteries required | no |
| Ageing resistance (UV) | good |
| Tensibility | 140 % |
| Tack | good |
| Chemical Resistance | very good |
| Humidity resistance | very good |
| Softener resistance | medium |
| Temperature resistance long term | 176 °F
80 °C |
| Static shear resistance at 40°C | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 176 °F
80 °C |
Adhesion to Values
| Adhesion to ABS (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to ABS (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to Aluminium (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to Aluminium (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PC (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PC (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PE (initial) | 1.14 lbs/in
2 N/cm |
| Adhesion to PE (after 14 days) | 1.14 lbs/in
2 N/cm |
| Adhesion to PET (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PET (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PP (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PP (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PS (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PS (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PVC (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PVC (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to Steel (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to Steel (after 14 days) | 3.43 lbs/in
6 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to ABS (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to Aluminium (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to Aluminium (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PC (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PC (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PE (initial) | 1.14 lbs/in
2 N/cm |
| Adhesion to PE (after 14 days) | 1.14 lbs/in
2 N/cm |
| Adhesion to PET (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PET (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PP (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PP (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PS (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PS (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to PVC (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to PVC (after 14 days) | 3.43 lbs/in
6 N/cm |
| Adhesion to Steel (initial) | 3.43 lbs/in
6 N/cm |
| Adhesion to Steel (after 14 days) | 3.43 lbs/in
6 N/cm |
Additional Info
Liner variants:
Peel Adhesion:
Longterm dampening properties and temperature resistance have been certified by ift institute, Germany (Report no. 13-003011-PR02)
- PV0 brown glassine paper (71 µm/2.8 mils)
- PV10 red transparent PP film (120 µm/4.72 mils)
Peel Adhesion:
- Immediate: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
- After 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC, PE, PP
Longterm dampening properties and temperature resistance have been certified by ift institute, Germany (Report no. 13-003011-PR02)
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.