Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | translucent |
| Color of liner | white/red logo |
| Liner Type | glassine |
| Thickness of liner | 69 µm |
| Total thickness | 50 µm |
| Weight of liner | 80 g/m² |
tesa® 58372
50µm double sided PET flame retardant tape
Product Features
- Thickness: 50µm
- Flame retardant per UL 94 VTM-0 level
- Good bonding performance
Product description
tesa® 58372 is a translucent, double-sided PET tape equipped with flame retardant tackified acrylic adhesive.
The white/red logo glassine liner ensures it can be easily released without adhesive residue.
Product details and specifications
Product Features
- Thickness: 50µm
- Flame retardant per UL 94 VTM-0 level
- Good bonding performance
- High long-term reliability and aging resistance
- Good handling performance in converting process
- Conforming to RoHS, REACH
- Halogen-free
- Its ultra thinner PET backing offers excellent converting performance for purpose of lamination.
- The flame retardant acrylic adhesive gives this product unique anti-flaming property, and also a good bonding performance even after long-term storage conditions.
Application Fields
tesa® 58372 can be introduced for EV battery pack sealing when it laminated with foamto meet the flame retardant target for E-mobility market. It is also used for general mounting applications especially in the EV battery system and the other environment in automotive industry when it comes with anti-flaming requirement.
Product Construction
| Adhesive Type | tackified acrylic |
| Backing material | PET film |
| Color | translucent |
| Color of liner | white/red logo |
| Liner Type | glassine |
| Thickness of liner | 69 µm |
| Total thickness | 50 µm |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Static shear resistance at 23°C | good |
| Humidity resistance | good |
| Temperature resistance long term | 125 °C |
Properties / Performance Values
| Static shear resistance at 23°C | good |
| Humidity resistance | good |
| Temperature resistance long term | 125 °C |
Adhesion to Values
| Adhesion to ABS (initial) | 5.1 N/cm |
| Adhesion to ABS (after 3 days) | 7.1 N/cm |
| Adhesion to Aluminium (initial) | 6.3 N/cm |
| Adhesion to Aluminium (after 3 days) | 6.8 N/cm |
| Adhesion to ASTM (initial) | 7.1 N/cm |
| Adhesion to PC (initial) | 6.3 N/cm |
| Adhesion to PC (after 3 days) | 7.3 N/cm |
| Adhesion to PI (initial) | 5.9 N/cm |
| Adhesion to PI (after 3 days) | 7.4 N/cm |
| Adhesion to Steel (initial) | 7.1 N/cm |
| Adhesion to Steel (after 3 days) | 8.5 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 5.1 N/cm |
| Adhesion to ABS (after 3 days) | 7.1 N/cm |
| Adhesion to Aluminium (initial) | 6.3 N/cm |
| Adhesion to Aluminium (after 3 days) | 6.8 N/cm |
| Adhesion to ASTM (initial) | 7.1 N/cm |
| Adhesion to PC (initial) | 6.3 N/cm |
| Adhesion to PC (after 3 days) | 7.3 N/cm |
| Adhesion to PI (initial) | 5.9 N/cm |
| Adhesion to PI (after 3 days) | 7.4 N/cm |
| Adhesion to Steel (initial) | 7.1 N/cm |
| Adhesion to Steel (after 3 days) | 8.5 N/cm |
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.