Product Construction
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of tape | 75 µm |
Total thickness | 75 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
75µm reinforced water-based acrylic adhesive layer with PET scrim for mounting in automotive interiors
tesa® 66007 is a conformable transparent adhesive layer of water based acrylic reinforced with a PET scrim mesh.
Features:
1 very low total VOC values and no critical substances detectable
1 high initial tack and peel adhesion
1 high conformable design following 3D shapes
1 provides excellent conformability and stability
1 provides excellent initial adhesion to a wide variety of interior substrates
1 suitable for the bonding to nonpolar plastics, foams, felts and fabrics
1 the scrim provides a reinforcement of flexible substrates for improving converting efficiency and handling
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of tape | 75 µm |
Total thickness | 75 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of tape | 75 µm |
Total thickness | 75 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Suitable for rough surfaces | very good |
Suitable for die cutting | yes |
Temperature resistance max. | 170 °C |
Fogging | very good |
Tack | very good |
Low VOC | very good |
Temperature resistance min. | -40 °C |
Suitable for rough surfaces | very good |
Suitable for die cutting | yes |
Temperature resistance max. | 170 °C |
Fogging | very good |
Tack | very good |
Low VOC | very good |
Temperature resistance min. | -40 °C |
Adhesion to ABS (initial) | 11 N/cm |
Adhesion to ABS (after 3 days) | 12.2 N/cm |
Adhesion to PC (initial) | 11.2 N/cm |
Adhesion to PC (after 3 days) | 11.4 N/cm |
Adhesion to PE (initial) | 4 N/cm |
Adhesion to PE (after 3 days) | 4.5 N/cm |
Adhesion to PET (initial) | 10.1 N/cm |
Adhesion to PET (after 3 days) | 11 N/cm |
Adhesion to PP (initial) | 4.5 N/cm |
Adhesion to PP (after 3 days) | 11 N/cm |
Adhesion to PS (initial) | 9.4 N/cm |
Adhesion to PS (after 3 days) | 10.8 N/cm |
Adhesion to PVC (initial) | 8.8 N/cm |
Adhesion to PVC (after 3 days) | 11.7 N/cm |
Adhesion to Steel (initial) | 9.7 N/cm |
Adhesion to Steel (after 3 days) | 12.3 N/cm |
Adhesion to ABS (initial) | 11 N/cm |
Adhesion to ABS (after 3 days) | 12.2 N/cm |
Adhesion to PC (initial) | 11.2 N/cm |
Adhesion to PC (after 3 days) | 11.4 N/cm |
Adhesion to PE (initial) | 4 N/cm |
Adhesion to PE (after 3 days) | 4.5 N/cm |
Adhesion to PET (initial) | 10.1 N/cm |
Adhesion to PET (after 3 days) | 11 N/cm |
Adhesion to PP (initial) | 4.5 N/cm |
Adhesion to PP (after 3 days) | 11 N/cm |
Adhesion to PS (initial) | 9.4 N/cm |
Adhesion to PS (after 3 days) | 10.8 N/cm |
Adhesion to PVC (initial) | 8.8 N/cm |
Adhesion to PVC (after 3 days) | 11.7 N/cm |
Adhesion to Steel (initial) | 9.7 N/cm |
Adhesion to Steel (after 3 days) | 12.3 N/cm |