Product Construction
| Backing material | PVC film |
| Color | white |
| Colour of liner | brown |
| Thickness of liner | 69 µm |
| Total thickness | 295 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | paper |
| Weight of liner | 80 g/m² |
tesa® 4968
Double-sided filmic tape
Product description
tesa® 4968 is a white double-sided self-adhesive tape consisting of a PVC-backing and a tackified acrylic adhesive.
tesa® 4968 features especially:
- An outstanding adhesion level even to critical low surface energy materials such as PP and PE
- Immediate functionality of the laminated bond due to excellent initial tack
- Light and age-resistant acrylic adhesive
Product details and specifications
Application Fields
- Mounting of non-heated exterior car mirrors onto the holding plate
- Mounting of mouldings and decorative trim parts in the furniture industry
Product Construction
| Backing material | PVC film |
| Color | white |
| Colour of liner | brown |
| Thickness of liner | 69 µm |
| Total thickness | 295 µm |
| Type of adhesive | tackified acrylic |
| Type of liner | paper |
| Weight of liner | 80 g/m² |
Properties / Performance Values
| Elongation at break | 130 % |
| Tensile strength | 30 N/cm |
| Softener resistance | very good |
| Temperature resistance long term | 60 °C |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | medium |
| Humidity resistance | very good |
| Chemical resistance | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 70 °C |
| Ageing resistance (UV) | good |
| Tack | very good |
Properties / Performance Values
| Elongation at break | 130 % |
| Tensile strength | 30 N/cm |
| Softener resistance | very good |
| Temperature resistance long term | 60 °C |
| Temperature resistance min. | -40 °C |
| Static shear resistance at 40°C | medium |
| Humidity resistance | very good |
| Chemical resistance | good |
| Static shear resistance at 23°C | good |
| Temperature resistance short term | 70 °C |
| Ageing resistance (UV) | good |
| Tack | very good |
Adhesion to Values
| Adhesion to ABS (initial) | 13.1 N/cm |
| Adhesion to ABS (after 14 days) | 20 N/cm |
| Adhesion to Aluminium (initial) | 10.3 N/cm |
| Adhesion to Aluminium (after 14 days) | 20.7 N/cm |
| Adhesion to PC (initial) | 13.8 N/cm |
| Adhesion to PC (after 14 days) | 24.6 N/cm |
| Adhesion to PET (initial) | 9.6 N/cm |
| Adhesion to PET (after 14 days) | 12.7 N/cm |
| Adhesion to PP (initial) | 11 N/cm |
| Adhesion to PP (after 14 days) | 14.1 N/cm |
| Adhesion to PS (initial) | 11.9 N/cm |
| Adhesion to PS (after 14 days) | 18.2 N/cm |
| Adhesion to PVC (initial) | 10.6 N/cm |
| Adhesion to PVC (after 14 days) | 25.3 N/cm |
| Adhesion to Steel (initial) | 12.5 N/cm |
| Adhesion to Steel (after 14 days) | 21.2 N/cm |
Adhesion to Values
| Adhesion to ABS (initial) | 13.1 N/cm |
| Adhesion to ABS (after 14 days) | 20 N/cm |
| Adhesion to Aluminium (initial) | 10.3 N/cm |
| Adhesion to Aluminium (after 14 days) | 20.7 N/cm |
| Adhesion to PC (initial) | 13.8 N/cm |
| Adhesion to PC (after 14 days) | 24.6 N/cm |
| Adhesion to PET (initial) | 9.6 N/cm |
| Adhesion to PET (after 14 days) | 12.7 N/cm |
| Adhesion to PP (initial) | 11 N/cm |
| Adhesion to PP (after 14 days) | 14.1 N/cm |
| Adhesion to PS (initial) | 11.9 N/cm |
| Adhesion to PS (after 14 days) | 18.2 N/cm |
| Adhesion to PVC (initial) | 10.6 N/cm |
| Adhesion to PVC (after 14 days) | 25.3 N/cm |
| Adhesion to Steel (initial) | 12.5 N/cm |
| Adhesion to Steel (after 14 days) | 21.2 N/cm |
Additional Info
Liner variants:
PV0 brown glassine paper (71 µm)
PV6 red MOPP-film (80 µm)
PV0 brown glassine paper (71 µm)
PV6 red MOPP-film (80 µm)
tesa® products prove their impressive quality day in, day out in demanding conditions and are regularly subjected to strict controls. All technical information and data above mentioned are provided to the best of our knowledge on the basis of our practical experience. They shall be considered as average values and are not appropriate for a specification. Therefore tesa SE can make no warranties, expressed or implied, including, but not limited to any implied warranty of merchantability or fitness for a particular purpose. The user is responsible for determining whether the tesa® product is fit for a particular purpose and suitable for the user’s method of application. If you are in any doubt, our technical staff will be glad to support you.
Downloads
Download the files below for more technical details and information on this product.