Product Construction
Backing material | PET film |
Color | black |
Colour of liner | brown/blue logo |
Thickness of liner | 69 µm |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
205µm double sided black film tape - order number tesa® 59652
tesa® 4965 Black is a double-sided self-adhesive tape consisting of a black PET backing and a modified acrylic adhesive and is based on a patented and protected product formulation. Several products are equipped with this unique and high performing product design and together these products make up Team 4965. This double-sided film tape assortment helps to easily select the most efficient tape based on customer demands, products, and processes. tesa® 4965 Black can be ordered using order number tesa® 59652. Explore the benefits of the full tesa® 4965 assortment here: https://www.tesa.com/en-sg/industry/general-applications/mounting/team-4965-assortment
tesa® 4965 Black features:
Backing material | PET film |
Color | black |
Colour of liner | brown/blue logo |
Thickness of liner | 69 µm |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Backing material | PET film |
Color | black |
Colour of liner | brown/blue logo |
Thickness of liner | 69 µm |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Type of liner | paper |
Weight of liner | 80 g/m² |
Elongation at break | 50 % |
Tensile strength | 20 N/cm |
Static shear resistance at 40°C | very good |
Tack | good |
Temperature resistance long term | 100 °C |
Softener resistance | good |
Temperature resistance min. | -40 °C |
Chemical resistance | good |
Humidity resistance | very good |
Static shear resistance at 23°C | very good |
Ageing resistance (UV) | good |
Temperature resistance short term | 200 °C |
Elongation at break | 50 % |
Tensile strength | 20 N/cm |
Static shear resistance at 40°C | very good |
Tack | good |
Temperature resistance long term | 100 °C |
Softener resistance | good |
Temperature resistance min. | -40 °C |
Chemical resistance | good |
Humidity resistance | very good |
Static shear resistance at 23°C | very good |
Ageing resistance (UV) | good |
Temperature resistance short term | 200 °C |
Adhesion to ABS (initial) | 10.8 N/cm |
Adhesion to ABS (after 14 days) | 11.9 N/cm |
Adhesion to Aluminium (initial) | 10.2 N/cm |
Adhesion to Aluminium (after 14 days) | 12.6 N/cm |
Adhesion to PC (initial) | 12.2 N/cm |
Adhesion to PC (after 14 days) | 13.4 N/cm |
Adhesion to PE (initial) | 5.6 N/cm |
Adhesion to PE (after 14 days) | 6.6 N/cm |
Adhesion to PET (initial) | 9.8 N/cm |
Adhesion to PET (after 14 days) | 11.9 N/cm |
Adhesion to PP (after 14 days) | 8.8 N/cm |
Adhesion to PP (covered side, initial) | 6 N/cm |
Adhesion to PS (initial) | 10.4 N/cm |
Adhesion to PS (after 14 days) | 12.1 N/cm |
Adhesion to PVC (initial) | 9.6 N/cm |
Adhesion to PVC (after 14 days) | 12.8 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 14 N/cm |
Adhesion to ABS (initial) | 10.8 N/cm |
Adhesion to ABS (after 14 days) | 11.9 N/cm |
Adhesion to Aluminium (initial) | 10.2 N/cm |
Adhesion to Aluminium (after 14 days) | 12.6 N/cm |
Adhesion to PC (initial) | 12.2 N/cm |
Adhesion to PC (after 14 days) | 13.4 N/cm |
Adhesion to PE (initial) | 5.6 N/cm |
Adhesion to PE (after 14 days) | 6.6 N/cm |
Adhesion to PET (initial) | 9.8 N/cm |
Adhesion to PET (after 14 days) | 11.9 N/cm |
Adhesion to PP (after 14 days) | 8.8 N/cm |
Adhesion to PP (covered side, initial) | 6 N/cm |
Adhesion to PS (initial) | 10.4 N/cm |
Adhesion to PS (after 14 days) | 12.1 N/cm |
Adhesion to PVC (initial) | 9.6 N/cm |
Adhesion to PVC (after 14 days) | 12.8 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 14 N/cm |