Product Construction
Backing material | PET film |
Color | black |
Colour of liner | white with tesa logo |
Thickness of liner | 69 µm |
Total thickness | 300 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
Weight of liner | 80 g/m² |
300µm double sided black high performance filmic tape
tesa® 61315 is a black, double sided self-adhesive tape consisting of a thick black PET backing and a tackified acrylic adhesive.
Special features:
Backing material | PET film |
Color | black |
Colour of liner | white with tesa logo |
Thickness of liner | 69 µm |
Total thickness | 300 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
Weight of liner | 80 g/m² |
Backing material | PET film |
Color | black |
Colour of liner | white with tesa logo |
Thickness of liner | 69 µm |
Total thickness | 300 µm |
Type of adhesive | tackified acrylic |
Type of liner | glassine |
Weight of liner | 80 g/m² |
Elongation at break | 80 % |
Tensile strength | 140 N/cm |
Ageing resistance (UV) | very good |
Static shear resistance at 40°C | good |
Static shear resistance at 23°C | good |
Temperature resistance short term | 200 °C |
Temperature resistance long term | 100 °C |
Humidity resistance | very good |
Elongation at break | 80 % |
Tensile strength | 140 N/cm |
Ageing resistance (UV) | very good |
Static shear resistance at 40°C | good |
Static shear resistance at 23°C | good |
Temperature resistance short term | 200 °C |
Temperature resistance long term | 100 °C |
Humidity resistance | very good |
Adhesion to ABS (initial) | 16 N/cm |
Adhesion to ABS (after 14 days) | 19.5 N/cm |
Adhesion to ABS (covered side, initial) | 16 N/cm |
Adhesion to ABS (covered side, after 14 days) | 19.5 N/cm |
Adhesion to Glass (initial) | 22 N/cm |
Adhesion to Glass (after 14 days) | 23 N/cm |
Adhesion to PC (initial) | 23 N/cm |
Adhesion to PC (after 14 days) | 24 N/cm |
Adhesion to PC (covered side, after 14 days) | 25 N/cm |
Adhesion to PC (covered side, initial) | 22 N/cm |
Adhesion to PMMA (initial) | 22 N/cm |
Adhesion to PMMA (after 14 days) | 25 N/cm |
Adhesion to Steel (initial) | 20.3 N/cm |
Adhesion to Steel (after 14 days) | 24 N/cm |
Adhesion to Steel (covered side, after 14 days) | 25 N/cm |
Adhesion to Steel (covered side, initial) | 20.8 N/cm |
Adhesion to ABS (initial) | 16 N/cm |
Adhesion to ABS (after 14 days) | 19.5 N/cm |
Adhesion to ABS (covered side, initial) | 16 N/cm |
Adhesion to ABS (covered side, after 14 days) | 19.5 N/cm |
Adhesion to Glass (initial) | 22 N/cm |
Adhesion to Glass (after 14 days) | 23 N/cm |
Adhesion to PC (initial) | 23 N/cm |
Adhesion to PC (after 14 days) | 24 N/cm |
Adhesion to PC (covered side, after 14 days) | 25 N/cm |
Adhesion to PC (covered side, initial) | 22 N/cm |
Adhesion to PMMA (initial) | 22 N/cm |
Adhesion to PMMA (after 14 days) | 25 N/cm |
Adhesion to Steel (initial) | 20.3 N/cm |
Adhesion to Steel (after 14 days) | 24 N/cm |
Adhesion to Steel (covered side, after 14 days) | 25 N/cm |
Adhesion to Steel (covered side, initial) | 20.8 N/cm |