Product Construction
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
220µm reinforced water based acrylic adhesive layer with PET scrim for mounting in automotive interiors
tesa® 66022 is a conformable transparent adhesive layer of water based acrylic reinforced with a PET scrim mesh.
Features:
1 very low total VOC values and no critical substances detectable
1 high initial tack and peel adhesion
1 high conformable design following 3D shapes
1 provides excellent conformability and stability
1 provides excellent initial adhesion to a wide variety of interior substrates
1 suitable for the bonding to nonpolar plastics, foams, felts and fabrics
1 suitable for a certain gap filling due to thick adhesive layer
1 reliable adhesion performance for the whole vehicle life time
1 the scrim provides a reinforcement of flexible substrates for improving converting efficiency and handling
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Backing material | none |
Color | transparent |
Colour of liner | brown/blue logo |
Thickness of liner | 71 µm |
Thickness of tape | 220 µm |
Type of adhesive | water-based acrylic |
Type of liner | glassine |
Fogging | very good |
Suitable for rough surfaces | very good |
Temperature resistance max. | 200 °C |
Low VOC | very good |
Suitable for die cutting | yes |
Temperature resistance min. | -40 °C |
Tack | very good |
Fogging | very good |
Suitable for rough surfaces | very good |
Temperature resistance max. | 200 °C |
Low VOC | very good |
Suitable for die cutting | yes |
Temperature resistance min. | -40 °C |
Tack | very good |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 3 days) | 18 N/cm |
Adhesion to PC (initial) | 19.1 N/cm |
Adhesion to PC (after 3 days) | 19.4 N/cm |
Adhesion to PE (initial) | 9.2 N/cm |
Adhesion to PE (after 3 days) | 9 N/cm |
Adhesion to PET (initial) | 16.2 N/cm |
Adhesion to PET (after 3 days) | 18.1 N/cm |
Adhesion to PET fleece Headliner A (after 3 days) | 8 N/cm |
Adhesion to PET fleece Headliner A (initial) | 6 N/cm |
Adhesion to PP (initial) | 14 N/cm |
Adhesion to PP (after 3 days) | 16 N/cm |
Adhesion to PS (initial) | 17.7 N/cm |
Adhesion to PS (after 3 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 19.3 N/cm |
Adhesion to Steel (initial) | 12.3 N/cm |
Adhesion to Steel (after 3 days) | 17.3 N/cm |
Adhesion to ABS (initial) | 17 N/cm |
Adhesion to ABS (after 3 days) | 18 N/cm |
Adhesion to PC (initial) | 19.1 N/cm |
Adhesion to PC (after 3 days) | 19.4 N/cm |
Adhesion to PE (initial) | 9.2 N/cm |
Adhesion to PE (after 3 days) | 9 N/cm |
Adhesion to PET (initial) | 16.2 N/cm |
Adhesion to PET (after 3 days) | 18.1 N/cm |
Adhesion to PET fleece Headliner A (after 3 days) | 8 N/cm |
Adhesion to PET fleece Headliner A (initial) | 6 N/cm |
Adhesion to PP (initial) | 14 N/cm |
Adhesion to PP (after 3 days) | 16 N/cm |
Adhesion to PS (initial) | 17.7 N/cm |
Adhesion to PS (after 3 days) | 18.2 N/cm |
Adhesion to PVC (initial) | 12 N/cm |
Adhesion to PVC (after 3 days) | 19.3 N/cm |
Adhesion to Steel (initial) | 12.3 N/cm |
Adhesion to Steel (after 3 days) | 17.3 N/cm |
Download the files below for more technical details and information on this product.