Product Construction
Backing material | PET film |
Color | transparent |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Double-sided filmic tape with fingerlift
tesa® 6965 consists of a transparent PET-film and an adhesive system that combines good adhesion with high shear resistance. It is especially resistant to plasticizers and offers a secure bond even at elevated temperatures.
Backing material | PET film |
Color | transparent |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Backing material | PET film |
Color | transparent |
Total thickness | 205 µm |
Type of adhesive | tackified acrylic |
Elongation at break | 50 % |
Tensile strength | 20 N/cm |
Chemical resistance | good |
Temperature resistance long term | 100 °C |
Humidity resistance | very good |
Temperature resistance short term | 200 °C |
Temperature resistance min. | -40 °C |
Tack | good |
Softener resistance | good |
Static shear resistance at 40°C | very good |
Ageing resistance (UV) | good |
Static shear resistance at 23°C | very good |
Elongation at break | 50 % |
Tensile strength | 20 N/cm |
Chemical resistance | good |
Temperature resistance long term | 100 °C |
Humidity resistance | very good |
Temperature resistance short term | 200 °C |
Temperature resistance min. | -40 °C |
Tack | good |
Softener resistance | good |
Static shear resistance at 40°C | very good |
Ageing resistance (UV) | good |
Static shear resistance at 23°C | very good |
Adhesion to ABS (initial) | 10.3 N/cm |
Adhesion to ABS (after 14 days) | 12 N/cm |
Adhesion to Aluminium (initial) | 9.2 N/cm |
Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
Adhesion to PC (initial) | 12.6 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 5.8 N/cm |
Adhesion to PE (after 14 days) | 6.9 N/cm |
Adhesion to PET (initial) | 9.2 N/cm |
Adhesion to PET (after 14 days) | 9.5 N/cm |
Adhesion to PP (initial) | 6.8 N/cm |
Adhesion to PP (after 14 days) | 7.9 N/cm |
Adhesion to PS (initial) | 10.6 N/cm |
Adhesion to PS (after 14 days) | 12 N/cm |
Adhesion to PVC (initial) | 8.7 N/cm |
Adhesion to PVC (after 14 days) | 13 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 11.8 N/cm |
Adhesion to ABS (initial) | 10.3 N/cm |
Adhesion to ABS (after 14 days) | 12 N/cm |
Adhesion to Aluminium (initial) | 9.2 N/cm |
Adhesion to Aluminium (after 14 days) | 10.6 N/cm |
Adhesion to PC (initial) | 12.6 N/cm |
Adhesion to PC (after 14 days) | 14 N/cm |
Adhesion to PE (initial) | 5.8 N/cm |
Adhesion to PE (after 14 days) | 6.9 N/cm |
Adhesion to PET (initial) | 9.2 N/cm |
Adhesion to PET (after 14 days) | 9.5 N/cm |
Adhesion to PP (initial) | 6.8 N/cm |
Adhesion to PP (after 14 days) | 7.9 N/cm |
Adhesion to PS (initial) | 10.6 N/cm |
Adhesion to PS (after 14 days) | 12 N/cm |
Adhesion to PVC (initial) | 8.7 N/cm |
Adhesion to PVC (after 14 days) | 13 N/cm |
Adhesion to Steel (initial) | 11.5 N/cm |
Adhesion to Steel (after 14 days) | 11.8 N/cm |
Download the files below for more technical details and information on this product.